Print Email Facebook Twitter Influence of nickel precursors on the properties and performance of Ni impregnated zeolite 5A and 13X catalysts in CO2 methanation Title Influence of nickel precursors on the properties and performance of Ni impregnated zeolite 5A and 13X catalysts in CO2 methanation Author Wei, L. (TU Delft Large Scale Energy Storage) Haije, W.G. (TU Delft Large Scale Energy Storage) Kumar, Narendra (Åbo Akademi University) Peltonen, Janne (University of Turku) Peurla, Markus (University of Turku) Grenman, L.O.H. (Åbo Akademi University) de Jong, W. (TU Delft Large Scale Energy Storage) Date 2020 Abstract Zeolite 13X and 5A supported Ni catalysts were synthesized for CO2 methanation using the evaporation impregnation method. The influence of using different Ni precursors (nitrate, citrate, and acetate) as well as calcination temperatures on the catalyst properties and performance were investigated. XRD, SEM-EDX, TEM, STEM-EDX, N2 physisorption, H2-TPR, TPD-NH3 and TG/DTA were used for detailed characterization of the catalysts. The parent structure of the zeolites did not change during catalyst synthesis. Using nickel citrate and acetate resulted in smaller NiO particle size compared to nitrate. STEM-EDX results showed that all the Ni-precursor complexes entered more efficiently the 13X zeolite structure, which is mainly due to steric hindrance resulting from the smaller pore size of 5A. Methanation experiments revealed that the 13X catalysts synthesized using nickel citrate (5% Ni) displayed clearly higher activity, compared to the catalysts synthesized using nickel nitrate or nickel acetate. A 79% conversion at 320 °C was obtained with 100% selectivity towards CH4 and the catalyst showed excellent stability during 200 h testing. Overall, it can be concluded that the Ni precursor significantly influences the physico-chemical characteristics and catalytic properties of Ni 13X and Ni 5A zeolite catalysts in CO2 methanation: complex size and pore size matter. Subject 13X zeolite5A zeoliteCatalytic performanceCO methanation catalystMaterial propertiesNi precursor salt anions To reference this document use: http://resolver.tudelft.nl/uuid:0ebf0cf4-14ea-4482-9831-9cfafdb36ce4 DOI https://doi.org/10.1016/j.cattod.2020.05.025 ISSN 0920-5861 Source Catalysis Today, 362, 35-46 Part of collection Institutional Repository Document type journal article Rights © 2020 L. Wei, W.G. Haije, Narendra Kumar, Janne Peltonen, Markus Peurla, L.O.H. Grenman, W. de Jong Files PDF 1_s2.0_S0920586120303047_main.pdf 6.14 MB Close viewer /islandora/object/uuid:0ebf0cf4-14ea-4482-9831-9cfafdb36ce4/datastream/OBJ/view