Print Email Facebook Twitter GPR-assisted evaluation of probabilistic fatigue crack growth in rib-to-deck joints in orthotropic steel decks considering mixed failure models Title GPR-assisted evaluation of probabilistic fatigue crack growth in rib-to-deck joints in orthotropic steel decks considering mixed failure models Author Heng, J. (TU Delft Steel & Composite Structures; Shenzhen University) Zhou, Zhixiang (Shenzhen University) Zou, Yang (Chongqing Jiaotong University) Kaewunruen, Sakdirat (University of Birmingham) Date 2022 Abstract Rib-to-deck (RD) welded joints in orthotropic steel decks (OSDs) of bridges demonstrates two major fatigue failure models, including the toe-to-deck (TTD) cracking and root-to-deck (RTD) cracking. Generally, the sole failure model is employed in the fatigue assessment of RD joints, causing a hot dispute on the dominant failure model. In this paper, the fatigue crack growth (FCG) in RD joints has been evaluated considering uncertainties and mixed failure models. A probabilistic fatigue crack growth (PFCG) model is at first established for the RD joint, in which two crack-like initial flaws are assumed at the weld toe and root of the RD joint. After that, the gaussian process regression is used to assist and boost the PFCG simulation. Then, the PFCG model is implemented on a typical OSD with the random traffic model. Finally, the result of the PFCG model is discussed in detail, including the failure model, fatigue reliability and life prediction, and crack size evolution. It is revealed that both the TTD and RTD cracking models have a notable contribution to fatigue failure and could not be ignored. More crucial, a remarkable reduction can be observed in the fatigue reliability of RD joints when considering mixed failure models. This study not only highlights the influence of mixed failure models on the fatigue performance of welded joints, but also provide an insight into the application of novel machine learning tools in solving the traditional structural issue. Subject Gaussian process regressionMixed failure modelsOrthotropic steel deckProbabilistic fatigue crack growthRib-to-deck joint To reference this document use: http://resolver.tudelft.nl/uuid:5df90966-44ab-41ef-a011-f776749d0d54 DOI https://doi.org/10.1016/j.engstruct.2021.113688 Embargo date 2023-07-01 ISSN 0141-0296 Source Engineering Structures, 252, 1-16 Bibliographical note Green Open Access added to TU Delft Institutional Repository 'You share, we take care!' - Taverne project https://www.openaccess.nl/en/you-share-we-take-care Otherwise as indicated in the copyright section: the publisher is the copyright holder of this work and the author uses the Dutch legislation to make this work public. Part of collection Institutional Repository Document type journal article Rights © 2022 J. Heng, Zhixiang Zhou, Yang Zou, Sakdirat Kaewunruen Files PDF 1_s2.0_S0141029621017740_main.pdf 9.92 MB Close viewer /islandora/object/uuid:5df90966-44ab-41ef-a011-f776749d0d54/datastream/OBJ/view