Experimental characterization of chemical and physical performance of epoxy modified bitumen

Experimental characterization of chemical and physical performance of epoxy modified bitumen

Pipintakos, Georgios (TU Delft Civil Engineering and Geosciences)

Erkens, S. (graduation committee)
Schlangen, E. (graduation committee)
Liu, Xueyan (mentor)
Apostolidis, Panos (graduation committee)
van de Ven, Martin (graduation committee)
Houben, Lambert (graduation committee)

Delft University of Technology

2018-05-15

The increasing traffic load has led to the use of polymer modifiers in bituminous mixes in order to improve the performance and the durability of the pavement structures. Epoxy is a thermoset material which ensures enhanced fatigue performance and improved mechanical characteristics when used to modify bituminous materials. However, unlike conventional modification techniques, a series of experimental methods have to be conducted to evaluate the chemical- related phenomena occurring during the binder production and their effects on the performance of the epoxy modified bitumen. For this reason in this thesis, the utilization of epoxy modifiers was investigated at binder level.
Initially, the chemical hardening (curing) process of epoxy modified bitumens (EMBs) was investigated by means of Fourier Transform Infrared (FT-IR) spectrometer and Dynamic Shear Rheometer (DSR). Different combinations of hardening conditions for three epoxy modification levels were studied. Properties, such as modulus and viscosity, were utilized to determine the workability of EMB. At the same time, by using the FT-IR spectrometer, the functional groups of EMBs during the chemical reactions were identified for the understanding of polymerization in the epoxy components.
Additionally, the DSR device was utilized to determine the fatigue and tensile strength of EMBs. It was found that, with increasing the content of epoxy modifier, the fatigue life and tensile strength were increased significantly compared to an unmodified binder.
Finally, the age hardening (aging) of EMBs was evaluated at different time intervals. For the simulation of short-term aging on EMBs, a short-term oven aging method (STOA) was used. For long-term aging, simulations were performed in a pressure aging vessel (PAV) under constant pressure and temperature. The results of chemical characterization and rheological properties of the aged EMBs were obtained by using DSR and FT-IR and were compared to the unmodified bitumen.

epoxy modified bitumen
chemical hardening (curing)
performance
aging

http://resolver.tudelft.nl/uuid:6f6740a0-1e69-4fed-bf39-a880dbea4e06

2021-01-01

Student theses

master thesis

© 2018 Georgios Pipintakos