Bartelds, G. (author), Nederveen, A. (author)
A series of full depth honeycomb panels containing one craoked face sheet were tested to failure in bending. Failure was due to either craok extension in damaged face layer or buckling of compressive facing; the last mode occurred even when the compressed face layer was undamaged. No significant difference in residual strength in bending towards...
report 1973
document
't Hart, W.G.J. (author)
Some residual strength tests have been performed on 610 mm wide centre-cracked panels at a temperature of -50 C, in order to examine whether equal Ke values are obtained as for 300 mm wide panels, tested at -50°C. This work is a continuation of the residual strength investigation reported in NLR TR 76103 and NLR TR 75168.
report 1976
document
Vlieger, H. (author)
Residual strength tests were carried out on center-cracked panels with a 2024-T3 or 7075-T6 skin and provided with eccentric stiffeners of practical design. The stiffeners were riveted to the skin. The material of the stiffeners was 7075-T6. In some cases the stiffeners were combined with Ti-alloy crack stoppers. On the basis of the test results...
report 1976
document
Vlieger, H. (author)
Past experience has shown that during the operational life of an aircraft structure cracks or failures may arise in different structural components. In future designs the designer must be able on the one hand to restrict the occurrence of cracks by a careful detail design and on the other hand to guarantee some specified life of the aircraft if...
report 1976
document
't Hart, W.G.J. (author)
Residual strength tests have heen performed, on 300 mm wide centrecracked panels of various thicknesses, at room temperature and at -50 C. During the tests, stable crack growth was filmed and recorded with the electric potential method. Fracture toughness was determined using the method of Feddersen.
report 1976
document
't Hart, W.G.J. (author)
Fatigue tests on unidirectional Ca/ep composite material have been performed to investigate whether previous fatigue loading did influence the residual static strength. Residual strength tests were carried out on (0, ± 45)2s and (± 45)2s laminates, while for the (O, ± 45)2s laminate the influence of previous tensile fatigue loading on the...
report 1977
document
Bartelds, G. (author)
report 1978
document
Schijve, J. (author)
Paper presented at the 16th ICAP Conference, Brussels, 14 and 15 May 1979.
report 1979
document
Vlieger, H. (author)
This report presents results of residual strength calculations, carried out on cracked panel configurations of various designs and provided with bonded stiffeners. The calculations were carried out using the computer program BOND. The results of these calculations are compared with results of residual strength tests, performed on panels of...
report 1983
document
de Koning, A.U. (author)
This study deals with fracture mechanics aspects of mode 1 crack growth under montonically increasing (quasi-static) loads. Using the finite element method stable crack growth and the plastic deformation fields associated with this process are analyzed. A two parameter approach is proposed for a description of initiation and subsequent stable...
report 1985
document
't Hart, W.G.J. (author), Frijns, R.H.W.M. (author)
Constant amplitude tension-compression fatigue tests were performed on notched (± 45, 02, 90, 02)s coupon specimens of the composite systems T300/F593, T400H/6376, T800H//5245C and IM6/APC-2. Delamination damage growth as a function of the number of fatigue cycles was determined using the ultrasonic C-scan technique. Considering the resistance...
report 1989
document
Chen, D. (author)
report 1990
document
Chen, D. (author)
doctoral thesis 1991
document
Klein Breteler, M. (author)
report 1991
document
Vroeg, J.H. de (author)
report 1992
document
van der Hoeven, W. (author)
Residual strength tests were performed on ARALL panels consisting of ARALL3 (3/2) laminates with bonded-on doublers. In particular, the effect of the doubler geometry (shape and thickness) on the residual strength was investigated. Prior to residual strength testing all panels were fatigue loaded to create a realistic type of damage, i.e. cracks...
report 1992
document
Labonté, S. (author), Wiggenraad, J.F.M. (author)
A preliminary investigation is reported of the development of a Structure Relevant (SR-) specimen, which maintains the essential features of a stiffened panel configuration, in order to study damage growth behavior at limited cost. Several SR-specimens were fabricated, damage was applied, either through impacts or by the insertion of artificial...
report 1993
document
Wouters, J (author)
report 1993
document
Smith, G.M (author)
report 1994
document
Klein Breteler, M. (author)
report 1994