document
Wanhill, R.J.H. (author)
This paper concisely reviews and discusses (1) metallurgically cleaner alloys like -2124, 2048 and 7475, (2) potential application of 7000 series alloys in tension panels, (3) development of high strength stress corrosion resistant thick section materials like 7010, 7049 and 705O, (4) powder metallurgy 7000 series alloys with high strength and...
report 1977
document
Jacobs, F.A. (author), Schijve, J. (author), Tromp, P.J. (author)
Fatigue tests under flight-simulation loading have been performed on unnotched Alclad 2024-T3, anodised 2.0 mm thick sheet specimens, manufactured according to several machine-shop processes applied in the air craft industry. From the results it appears that milling is preferable to stamping. Rounding off the edges is also advantageous. The...
report 1977
document
't Hart, W.G.J. (author)
Fatigue tests on unidirectional Ca/ep composite material have been performed to investigate whether previous fatigue loading did influence the residual static strength. Residual strength tests were carried out on (0, ± 45)2s and (± 45)2s laminates, while for the (O, ± 45)2s laminate the influence of previous tensile fatigue loading on the...
report 1977
document
't Hart, W.G.J. (author)
Residual strength tests have heen performed, on 300 mm wide centrecracked panels of various thicknesses, at room temperature and at -50 C. During the tests, stable crack growth was filmed and recorded with the electric potential method. Fracture toughness was determined using the method of Feddersen.
report 1976
document
van Leeuwen, H.P. (author), Schra, L. (author)
The literature is reviewed with respect to: - tests conducted to investigate crack re-initiation under dynamic load and arrest of a running crack - metallurgical sources of rate effects - available data for aerospace engineering materials - mechanical sources of rate effects, i.e. dynamic crack tip stresses and kinetic energy effects Conclusions...
report 1975
document
't Hart, W.G.J. (author), Nederveen, A. (author), Stoffels, E. (author), Tromp, J. (author)
Residual strength tests have been performed on 610 mm wide centre cracked panels. During the tests, stable crack growth was filmed and crack opening displacements were measured. Fracture toughness was determined using the method of Feddersen. Flight simulation fatigue tests were carried out to investigate the crack propagation properties. A...
report 1975