The effect of sheet edge working on the fatigue life under flight-simulation loading

Fatigue tests under flight-simulation loading have been performed on unnotched Alclad 2024-T3, anodised 2.0 mm thick sheet specimens, manufactured according to several machine-shop processes applied in the air craft industry. From the results it appears that milling is preferable to stamping. Rounding off the edges is also advantageous. The...

Flight-simulation tests on notched elements

Tests were carried out on open-hole specimens, lugs and riveted strap joints of 2024-T3 and 7075-T6 materials. The effects of design stress level, truncating high-amplitude gust loads and omitting low-amplitude gust cycles were stuaied. Observations of the open-hole specimens include data on crack initiation, crack closure and damage increments....

Fatigue damage accumulation and incompatible crack front orientation