Flight simulation fatigue crack growth testing of aluminium alloys: Specific issues and guidelines

Flight simulation fatigue crack growth tests are necessary for verification of aircraft damage tolerance analyses and crack growth prediction methods, and also for comparing candidate materials for aircraft structural applications. However, such tests involve complicating issues that have emerged from many investigations on aluminium alloys...

Damage tolerance and durability evaluation of aluminium-lithium alloys

New impetus to continued use of alximinium alloys in major structural areas of aircraft has been given by the development of aluminium-lithium alloys. However, qualification of these new materials for service requires extensive testing and evaluation, preferably in international cooperative programmes. The evaluation of aluminium-lithium alloys...

Engineering property comparisons of PM and IM aluminium alloy forgings

Engineering properties of the PM alloy 7091-T7E69 and the IM alloys 7075-T73, 7175-T736, 7010-T736 and 7050-T736 were compared. The properties considered were strength, fracture toughness, fatigue strength, fatigue crack propagation resistance under constant amplitude and spectrum loading, stress corrosion crack initiation and propagation...

Effects of crack plane orientation transitions on flight simulation fatigue crack propagation in a high strength aluminium alloy (7050)

The effects of flat to slant fracture transitions on flight simulation fatigue crack propagation in specimens of 7O5O aluminium alloy forgings are discussed. For specimens containing flat, shearlipped, or full slant fractures at similar crack lengths the crack resistance (R curve) approach appears to provide an explanation for differences in the...

The effects of peening and hole expansion on the fatigue behaviour of 7079-T652 aluminium alloy

The effects of shot and glass bead peening and hole expansion on the direct stress fatigue life of 7079-1'652 aliiminium alloy specimens are considered. Three types of specimens were employed: unnotched, notched by a central hole and notched at comers. Shot peening was only slightly beneficial for high cycle fatigue, and then only for comer...