Uncovering the white etching area and crack formation mechanism in bearing steel

The microstructure of a damaged bearing from the field was characterized in this work with the intention to better understand microstructural features behind formation of White Etching Cracks (WEC) in bearings. Microstructural characterization of the altered white etching area (WEA) involved conventional electron backscattered diffraction ...

Confirming Debonding of Non-Metallic Inclusions as an Important Factor in Damage Initiation in Bearing Steel

Damage in bearings is closely associated with the presence of microstructural alterations, known as white etching areas (WEAs) and white etching cracks (WECs). One of the main reasons for the creation of these microstructural alterations is the presence of defects in the material, such as non-metallic inclusions. Manganese sulfides and...

The effect of Nb on the hydrogen embrittlement susceptibility of Q&P steel under static and dynamic loading

In the present study, the effect of Niobium (Nb) on the hydrogen embrittlement resistance of Quenched and Partitioning (Q&P) steel is investigated. For this purpose, the hydrogen uptake level and its impact on the mechanical properties of a Nb-free and a 0.024 wt% Nb Q&P steel are thoroughly analysed. The hydrogen trapping capacity is...