Stepniowski, W.J. (author), Moneta, Marcin (author), Karczewski, Krzysztof (author), Michalska-Domanska, Marta (author), Czujko, Tomasz (author), Mol, J.M.C. (author), Buijnsters, J.G. (author)
Anodic aluminum oxide was formed by employing mild and hard anodizing in sulfuric acid followed by mild anodizing in oxalic acid without oxide removal in-between at 40 and 45 V. Such multi-step anodizing, combining hard anodizing in sulfuric acid with mild anodizing in oxalic acid allowed to form a highly-ordered nanoporous template with a...
journal article 2018
Stepniowski, W.J. (author), Stojadinović, Stevan (author), Vasilić, Rastko (author), Tadić, Nenad (author), Karczewski, Krzysztof (author), Abrahami, S.T. (author), Buijnsters, J.G. (author), Mol, J.M.C. (author)
Copper foil was anodized in 1 M KOH at potentials ranging from −400 to −100 mV vs. Ag|AgCl electrode. Cyclic voltammetry showed a distinct peak with a maximum at around −150 mV. For anodizing at −100 and −200 mV, nanowires with diameters of ca. 19 and 24 nm respectively were found to be grown. Moreover, photoluminescence and X-ray diffraction...
journal article 2017