Expansion and degradation of cement paste in sodium sulfate solutions

External sulfate attack is a progressive degradation process that may cause expansion, cracking, loss of binder cohesion and increased permeability in cementitious materials. Crystallization pressure theory has often been referred to as the most likely mechanism. However, thus far the stress causing the expansion has not been quantified. In...

Experimental and numerical study on cement paste degradation under external sulfate attack

External sulfate attack is one of the situations that may cause gradual but severe damage in cementitious materials, which may lead to cracking, increased permeability and strength loss. In this paper, thin-walled hollow cement paste cylinders with a wall thickness of 2.5mm were made considering the slow penetration process of sulfate ions under...