Prediction of the nonlinear dynamic behaviour of a concrete slab subjected to blast load

With the rise of hydrogen as a green alternative for fossil fuels, the demand for storage capacity of hydrogen increases significantly. Due to the high risk of explosions in urban environments it brings along, the blast analysis of buildings within in range of the explosions becomes more relevant.<br/><br/>The goal of this research is to develop...

Autogenous shrinkage of early age cement paste and mortar

Concrete is a brittle composite material that easily fractures under tension. Due to the fact that the early-age deformation of the concrete member is restrained by adjoining structures, cracking can occur throughout the concrete prior to application of any load. The cracks would provide preferential access for aggressive agents penetrating in...

Effects of slag and fly ash on reinforcement corrosion in concrete in chloride environment: Research from the Netherlands

A review is given of research on the durability performance of concrete made with blast furnace slag and fly ash related to chloride induced reinforcement corrosion, carried out in the Netherlands, where slag has been used in cement for almost a century. Results are presented from field studies on concrete in marine environment and laboratory...

Autogenous Shrinkage of Cementitious materials containing BFS

In the Netherlands blast furnace slag (BFS) cement is commonly used. Concretes with this type of cement are known for good durability properties. Where concrete is designed to crack in order to let the incorporated steel reinforcement take over tensile stresses, it is mainly for durability reasons that non-designed cracking of concrete is...