Kolkman, H.J. (author)Differences in the fatigue crack propagation rates of 2024-T351 and 2324-T39 are explicable from differences in microstructures. The slope changes (transitions) in the crack propagation curves are probably associated with the plastic zone sizes being equal to certain microstructural dimensions. As a consequence of different chemical compostion...report 1985
- document
-
't Hart, W.G.J. (author)Fatigue tests on unidirectional Ca/ep composite material have been performed to investigate whether previous fatigue loading did influence the residual static strength. Residual strength tests were carried out on (0, ± 45)2s and (± 45)2s laminates, while for the (O, ± 45)2s laminate the influence of previous tensile fatigue loading on the...report 1977
- document
-
Schijve, J. (author), Jacobs, F.A. (author), Tromp, P.J. (author)Flight-simulation tests were carried out on sheet specimens notched "by an open hole (Kt = 2.66). The material was 2024-T3 in three conditions; Alclad, bare and chemically milled. The crack initiation period and the crack propagation period were considerably shorter for the Alclad material. The significance of the cladding, both for constant...report 1976
- document
-
't Hart, W.G.J. (author), Nederveen, A. (author), Stoffels, E. (author), Tromp, J. (author)Residual strength tests have been performed on 610 mm wide centre cracked panels. During the tests, stable crack growth was filmed and crack opening displacements were measured. Fracture toughness was determined using the method of Feddersen. Flight simulation fatigue tests were carried out to investigate the crack propagation properties. A...report 1975