Multiple-site damage crack growth behaviour in Fibre Metal Laminate structures

Fibre metal laminates (FMLs)were developed and refined for their superior crack growth resistance and critical damage size that complimented the damage tolerance design philosophy utilized in the aerospace sector. Robust damage tolerance tools have been developed for FMLs. However, they tend to focus on the evolution of an isolated crack. There...

An experimental investigation into pin loading effects on fatigue crack growth in Fibre Metal Laminates

This paper provides an experimental investigation into the pin loading effects on the crack growth behaviour in Fibre Metal Laminates. The pin loading effects and bypass loading effects are incorporated in two different tested joints. The analysis of the test results shows that pin loading dominates the crack growth only in the vicinity of the...

Fatigue Crack and Delamination Growth in Fibre Metal Laminates under Variable Amplitude Loading

This thesis presents the investigation into the fatigue propagation and delamination growth of Fibre Metal Laminates under variable amplitude loading. As explained in the first chapter, the motivation of the research is twofold: first, to obtain a clear understanding and detailed characterization of the failure mechanisms in GLARE under variable...