Heat treatment studies of aluminium alloy type 7050 forgings. Interim report no. 3: Corroded-specimen fatigue tests and SCC propagation tests

The influence of previous corrosion on the fatigue life was investigated. It was foimd that a slight corrosive attack could drastically reduce the fatigue life. The damaging effect of corrosion was greater for the alloy AA 7050 than for AZ 74.61. It could be established that fatigue cracks initiated from various corrosion pits. A second series...

Heat treatment studies of aluminium alloy forgings of the AZ 74.61 type. Interim report no. 3: Fatigue crack propagation performance under manoeuvre spectrum loading

The fatigue crack propagation performance of the alloy AZ 74.61 under manoeuvre spectrum loading was studied. The crack propagation behaviour was also compared with that of the American forging alloy AA 7050, not only for simulated manoeuvre loading but also for simulated gust loading and programme loading. It was found that, at comparable...

Heat treatment studies of aluminium alloy type 7050 forgings. Interim report no. 2: The effect of heat treatment on a variety of engineering properties

The effect of variety of heat treatments on various engineering properties was studied with the aim to derive an optimum heat treatment. The engineering properties comprised Vickers hardness, short-time tensile strength, fatigue crack propagation resistance, fracture toughness and stress corrosion resistance. The test results were compared with...