Experimental quality assessment of thermoplastic composite corner regions manufactured using laser-assisted tape placement

Over the past 25 years, interest in thermoplastic composites in aircraft has steadily increased. Combining winding and laser-assisted tape placement is a promising method to manufacture thermoplastic structures using in-situ consolidation, as shown recently by manufacturing a variable stiffness, unitized, integrated-stiffener thermoplastic...

Novel thermomechanical characterization for shrinkage evolution of unidirectional semi-crystalline thermoplastic prepregs (PPS/CF) in melt, rubbery and glassy states

Shrinkages, distortions and high residual stresses in the thermoplastic composite parts are induced due to high processing temperature, anisotropy, and fiber–matrix shrinkage mismatch. In this paper the shrinkages have been investigated experimentally and modeled by thermo-mechanical constitutive equations for PolyPhenylene Sulfide (PPS) and...

On the sensitivity of ultrasonic welding of epoxy- to polyetheretherketone (PEEK)-based composites to the heating time during the welding process

This study aims at assessing the sensitivity of the ultrasonic welding process for joining epoxy- to thermoplastic-based composites sensitivity to the heating time. For that, carbon fibre (CF)/epoxy adherends with a co-cured PEI coupling layer were ultrasonically welded to CF/polyetheretherketone (PEEK) adherends at different heating times....

On the sensitivity of the ultrasonic welding process of epoxy- to polyetheretherketone (PEEK)-based composites to the welding force and amplitude of vibrations

This paper addresses the sensitivity of the ultrasonic welding process for joining dissimilar composites to variations in either the welding force or amplitude of vibrations. For that, carbon fibre (CF)/epoxy specimens were welded to CF/polyetheretherketone (PEEK) specimens, through a polyetheretherimide (PEI) coupling layer co-cured with the...

Resin Transfer molding of High-Fluidity Polyamide-6 with modified Glass-Fabric preforms

In Resin Transfer Molding (RTM), resin precursors of thermoset or, more recently, thermoplastic polymers are generally employed, raising issues related to the chemical reaction taking place during and after part processing. In this study, already polymerized polyamide-6 with low melt-viscosity (~30 Pa·s at 280 °C), is injected at low pressure...

Morphology of ply drops in thermoplastic composite materials manufactured using laser-assisted tape placement

Mechanical properties of composite laminates can be tuned by either tailoring ply orientations or by using ply drops to change thickness profiles. The latter cause resin-rich pockets to form in thermoset composites that are autoclave cured after lay-down. This paper focuses on the morphology of ply drop regions with carbon fibre thermoplastic...

Hygrothermal viscoelastic material characterisation of unidirectional continuous carbon-fibre reinforced polyamide 6

This paper presents results of material characterisation experiments on the hygrothermal viscoelastic behaviour of unidirectional laminates of continuous carbon-fibre reinforced polyamide 6. The material behaviour when subjected to the automotive painting process is of interest. Coefficients of thermal- and -moisture expansion were determined...

A study on amplitude transmission in ultrasonic welding of thermoplastic composites

Ultrasonic welding of thermoplastic composite materials is a promising joining technique that is now moving towards up-scaling, i.e. the assembling of large industrial parts. Despite its growing technological maturation, the assumed physical mechanisms underlying ultrasonic heating (viscoelastic heating, friction) are still insufficiently...

Towards robust sequential ultrasonic spot welding of thermoplastic composites: Welding process control strategy for consistent weld quality

The research in this paper is an essential part of a bigger effort on developing robust sequential ultrasonic welding of multi-spot welded joints in thermoplastic composites. It mainly focused on assessing the impact of the changes in boundary conditions on the welding process and whether it could be circumvented by using an appropriate...

Ultrasonic welding of carbon/epoxy and carbon/PEEK composites through a PEI thermoplastic coupling layer

This paper investigates welding of carbon/epoxy and carbon/PEEK composites using the following procedure. Firstly, the carbon/epoxy composite was made “weldable” through a very thin PEI thermoplastic film co-cured on its surface. During the curing cycle, the PEI resin and the components of the epoxy resin system partially diffused into each...

Mechanical behaviour of thermoplastic composites spot-welded and mechanically fastened joints: A preliminary comparison

The in-plane and out-of-plane mechanical behaviour of both ultrasonically spot-welded and mechanically fastened joints was investigated by double-lap shear and pull-through tests, respectively. Spot-welded specimens showed comparable onset failure load and significantly higher joint stiffness compared to mechanical fasteners when carrying shear...

Zero-flow: A novel approach to continuous ultrasonic welding of CF/PPS thermoplastic composite plates

Continuous ultrasonic welding of plastic films, fabrics, and even thermoplastic composite prepreg tape is a common industrial practice. However, continuous ultrasonic welding of stiff thermoplastic composite plates is challenging due to squeeze flow of resin at the welding interface, and significant local deformation of the welding stack, that...

A study of process induced voids in resistance welding of thermoplastic composites

Void formation in resistance welding of woven fabric reinforced thermoplastic composites was investigated. Void contents were measured using optical microscopy and digital image process. Un-even void distributions were observed in the joints, and more voids were found in the middle of the joints than the edges. A higher welding pressure was...

Effect of cooling rate on interlaminar fracture energy and shear strength of APC-2 laminates

The effect of cooling rate on some mechanical properties of APC-2/AS4 composite was investigated over the range between 1 and 70° C/min. Preconsolidated unidirectional laminates were reprocessed in a hot platen press at controlled cooling rates. Double Cantilever Beam specimens and End Notch Flexure specimens were used to determine the mode I...