Nederveen, A. (author), de Jong, J.B. (author)The influence of the approximation of the lower end of the load spectrum was investigated by comparative tests using the Basic F-27 test programme and an extended version, containing three times more cycles per flight. Crack growth was studied on notched sheet specimens made of Alclad 202U-T3 and Alclad TOT5-T6. Fatigue life tests were done on...report 1981
- document
-
van der Hoeven, W. (author), Schra, L. (author)The influence of sheet thickness (2 mm and 10 mm) and the influence of laminating (5x2 ram) on the fatigue crack growth properties of the aluminium alloy AL 7010-T 73651 were investigated. Both constant amplitude loading and flight simulation loading were applied. All 2 mm and 10 mm thick sheets were machined from a 150 mm thick plate, i.e....report 1981
- document
-
van der Linden, H.H. (author)The report describes a joint Garteur activity in the field of the prediction of crack propagation under variable amplitude loading. Existing crack propagation models or models under development will be checked with NLR crack propagation data of 202U-T3 Alclad 2 mm sheet material under F-27 Spectrum flight simulation loading. After completion of...report 1979
- document
-
de Koning, A.U. (author)In the present report a simple analytical model for the "behaviour of a centrally cracked strip is proposed. Formulae for computation of compliance, crack opening displacement and effective crack extension force are derived. The model is based on the classical solution for a crack infinite sheet under uniaxial tension. The effect of finite...report 1979
- document
-
't Hart, W.G.J. (author), Schra, L. (author)An experimental investigation.was performed on 80 mm thick plate material of 7OIO-T7651 and 7OIO-T73651 developed by Alcan Industries Ltd in U.K. The testing programme involved: tensile tests, fracture toughness, stress corrosion and fatigue tests. For comparison a similar investigation vas carried out on 7075-T7351 Alcoa plate material.report 1979