Predicting the Structural Performance of Composite Structures Under Cyclic Loading

The increased use of advanced composite materials on primary aircraft structure has brought back to the forefront the question of how such structures perform under repeated loading. In particular, when damage or other stress risers are present, tests have shown that the load to cause failure after a given number of cycles is a decreasing...

A damage tolerance study conducted with structure relevant specimens

A preliminary investigation is reported of the development of a Structure Relevant (SR-) specimen, which maintains the essential features of a stiffened panel configuration, in order to study damage growth behavior at limited cost. Several SR-specimens were fabricated, damage was applied, either through impacts or by the insertion of artificial...

Fatigue and residual strength behaviour of ARALL3 panels with bonded-on doublers

Residual strength tests were performed on ARALL panels consisting of ARALL3 (3/2) laminates with bonded-on doublers. In particular, the effect of the doubler geometry (shape and thickness) on the residual strength was investigated. Prior to residual strength testing all panels were fatigue loaded to create a realistic type of damage, i.e. cracks...

Delamination growth in improved carbon composites under constant amplitude fatigue loading

Constant amplitude tension-compression fatigue tests were performed on notched (± 45, 02, 90, 02)s coupon specimens of the composite systems T300/F593, T400H/6376, T800H//5245C and IM6/APC-2. Delamination damage growth as a function of the number of fatigue cycles was determined using the ultrasonic C-scan technique. Considering the resistance...

Review of aeronatical fatigue investigations in the Netherlands during the period march 1977 - february 1979

Paper presented at the 16th ICAP Conference, Brussels, 14 and 15 May 1979.

Residual strength characteristics of composite reinforced stiffened panels

Residual strength properties of carbon/epoxy composite material

Fatigue tests on unidirectional Ca/ep composite material have been performed to investigate whether previous fatigue loading did influence the residual static strength. Residual strength tests were carried out on (0, ± 45)2s and (± 45)2s laminates, while for the (O, ± 45)2s laminate the influence of previous tensile fatigue loading on the...