Damage accumulation analysis of cfrp cross-ply laminates under different tensile loading rates

This paper investigates the loading rate effect on both mechanical properties and damage accumulation process of [0°2/90°4]S carbon fiber-polymer laminates under tensile loading. In-situ edge observations, Acoustic Emission and Digital Image Correlation techniques were utilized simultaneously to monitor the state of damage in real time. Results...

Damage assessment of a titanium skin adhesively bonded to carbon fiber–reinforced plastic omega stringers using acoustic emission

This study is devoted to the use of acoustic emission technique for a comprehensive damage assessment, that is, damage detection, localization, and classification, of an aeronautical metal-to-composite bonded panel. The structure comprised a titanium panel adhesively bonded to carbon fiber–reinforced plastic omega stringers. The panel contained...

Unfolding the early fatigue damage process for CFRP cross-ply laminates

This study investigates the early fatigue damage of cross-ply carbon/epoxy laminates. The aim is to unfold the damage accumulation process, understand the interaction between different damage mechanisms, and quantify their contribution to stiffness degradation. Tension-tension fatigue tests were performed, while edge observation and DIC...

In-situ fatigue damage assessment of carbon-fibre reinforced polymer structures using advanced experimental techniques

This study focused on the in-situ fatigue damage assessment of open-hole carbon/epoxy coupons using Acoustic Emission (AE) and Digital Image Correlation (DIC) techniques. Constant amplitude fatigue tests were performed and the main objective was to investigate the damage process, the degradation process of the fatigue modules and to identify...