Residual strength of cracked 7075 T6 Al-alloy sheets under high loading rates

Constant-amplitude and flight-simulation fatigue tests on adhesive bonded lap joint specimens of 2024-T3 sheet material

Fatigue tests were carried out on Redux and FM 123/5 bonded specimens at various stress levels, temperatures (RT to 65 C) and low and high test frequencies. Observations were made on the type of failure (bond line failure or sheet failure) and the significance of the adhesive squeezeout for crack nucleation. An analysis of the data and a...

Some tests to assess the effect of crack stoppers on the fatigue life of centre-notched sheetspecimens

Several simple crack stopping methods were evaluated In fatigue crack propagation tests on 2024-T3 Alclad sheet specimens. After precracklng until a crack of 40 mm was obtained crack stoppers were Installed and the fatigue test was continued. Crack stoppers Installed In stop holes were: a blind rivet, a hard driven rivet, a heavily tightened...

Review of aeronatical fatigue investigations in the Netherlands during the period march 1977 - february 1979

Paper presented at the 16th ICAP Conference, Brussels, 14 and 15 May 1979.

Een tweede serie orienterende geluidsvermoeiingsproeven op een triltafel

A second series of exploratory acoustic fatigue tests using a shaker. A second series of exploratory acoustic fatigue tests was carried out, again employing simple specimens mounted on a shaker. Strain measurements were compared with calculations. Crack growth initiated by a central notch was observed. A comparison was made between three types...

Environmental effects on crack grwoth in flight-simulation tests on 2024-T3 and 7075-T6 material Supplement: Compilation of test data from an investigation on the effect of environment on crack growth under flight-simulation loading

Flight-simulation tests based on a standardized gust load spectrum were carried out in normal air, very dry air and salt water. Specimen thicknesses were t = 2 mm and t = 10 mm, mean stress in flight was 70 or 55 MN/m². In all cases a significant effect of the environment was found. Fatigue lives for t = 10 ram were much shorter than for t = 2...

The significance of cladding for fatigue of aluminium alloys in aircraft structures

Flight-simulation tests were carried out on sheet specimens notched "by an open hole (Kt = 2.66). The material was 2024-T3 in three conditions; Alclad, bare and chemically milled. The crack initiation period and the crack propagation period were considerably shorter for the Alclad material. The significance of the cladding, both for constant...

Fatigue damage accumulation and incompatible crack front orientation