Effect of ultra-fast heat treatment on the subsequent formation of mixed martensitic/bainitic microstructure with carbides in a crmo medium carbon steel

The current work focuses on complex multiphase microstructures gained in CrMo medium carbon steel after ultra-fast heat treatment, consisting of heating with heating rate of 300 C/s, 2 s soaking at peak temperature and subsequent quenching. In order to better understand the microstructure evolution and the phenomena that take place during...

The effect of ultra-fast heating on the microstructure, grain size and texture evolution of a commercial low-C, medium-Mn DP steel

The effect of ultra-fast heating on the microstructures of steel has been thoroughly studied over the last year as it imposes a suitable alternative for the production of ultra high strength steel grades. Rapid reheating followed by quenching leads to fine-grained mixed microstructures. This way the desirable strength/ductility ratio can be...

Study of carbide dissolution and austenite formation during ultra–fast heating in medium carbon chromium molybdenum steel

In this study, UltraFast Heat Treatment (UFHT) was applied to a soft annealed medium carbon chromium molybdenum steel. The specimens were rapidly heated and subsequently quenched in a dilatometer. The resulting microstructure consists of chromium-enriched cementite and chromium carbides (in sizes between 5–500 nm) within fine (nano-sized)...

The effect of ultrafast heating on cold-rolled low carbon steel: Formation and decomposition of austenite

The effect of heating rate on the formation and decomposition of austenite was investigated on cold-rolled low carbon steel. Experiments were performed at two heating rates, 150 ˚C/s and 1500 ˚C/s, respectively. The microstructures were characterized by means of scanning electron microscopy (SEM) and electron backscattered diffraction (EBSD)....