document
Schra, L. (author), 't Hart, W.G.J. (author)
Engineering property comparisons have been made for plate material of the newly developed aluminium alloy 2324-T39 and the widely used alloy 2024-T351. The properties considered were: tensile strength, fracture toughness, notched fatigue strength, and the resistance to fatigue crack propagation under both constant amplitude and flight simulation...
report 1984
document
't Hart, W.G.J. (author)
An experimental investigation was performed to examine the effect of low energy impact damage on tension-compression fatigue properties of sandwich panels. The specimens consisted of a 9 mm thick Nomex honeycomb and face sheets of (0,± 45) and (± 45,0) Carbon/epoxy. Drop weight impact was applied to create internal laminate damage. In order to...
report 1981
document
't Hart, W.G.J. (author), Schra, L. (author)
An experimental investigation.was performed on 80 mm thick plate material of 7OIO-T7651 and 7OIO-T73651 developed by Alcan Industries Ltd in U.K. The testing programme involved: tensile tests, fracture toughness, stress corrosion and fatigue tests. For comparison a similar investigation vas carried out on 7075-T7351 Alcoa plate material.
report 1979
document
't Hart, W.G.J. (author)
Residual strength tests have been carried out on various Kevlar 49-Carbon epoxy laminate configurations consisting of a carbon/epoxy core with face sheets of Kevlar 49 fabric. The influence of fatigue loading of notched specimens on the residual strength was investigated.
report 1978
document
't Hart, W.G.J. (author)
report 1977
document
't Hart, W.G.J. (author)
Fatigue tests on unidirectional Ca/ep composite material have been performed to investigate whether previous fatigue loading did influence the residual static strength. Residual strength tests were carried out on (0, ± 45)2s and (± 45)2s laminates, while for the (O, ± 45)2s laminate the influence of previous tensile fatigue loading on the...
report 1977
document
't Hart, W.G.J. (author)
Residual strength tests have heen performed, on 300 mm wide centrecracked panels of various thicknesses, at room temperature and at -50 C. During the tests, stable crack growth was filmed and recorded with the electric potential method. Fracture toughness was determined using the method of Feddersen.
report 1976
document
't Hart, W.G.J. (author)
A microscopic study has been performed on carbon composite fracture surfaces, using the Scanning Electron Microscope (SEM). It appears that the SEM is a useful tool to examine the fracture surface characteristics of composite materials failing under different loading conditions.
report 1976
document
't Hart, W.G.J. (author), Nederveen, A. (author), Stoffels, E. (author), Tromp, J. (author)
Residual strength tests have been performed on 610 mm wide centre cracked panels. During the tests, stable crack growth was filmed and crack opening displacements were measured. Fracture toughness was determined using the method of Feddersen. Flight simulation fatigue tests were carried out to investigate the crack propagation properties. A...
report 1975
document
't Hart, W.G.J. (author), Jacobs, F.A. (author), Nassette, J.H. (author)
report 1975