Fabrication of copper nanowires via electrodeposition in anodic aluminum oxide templates formed by combined hard anodizing and electrochemical barrier layer thinning

Anodic aluminum oxide was formed by employing mild and hard anodizing in sulfuric acid followed by mild anodizing in oxalic acid without oxide removal in-between at 40 and 45 V. Such multi-step anodizing, combining hard anodizing in sulfuric acid with mild anodizing in oxalic acid allowed to form a highly-ordered nanoporous template with a...

Morphology and photoluminescence of nanostructured oxides grown by copper passivation in aqueous potassium hydroxide solution

Copper foil was anodized in 1 M KOH at potentials ranging from −400 to −100 mV vs. Ag|AgCl electrode. Cyclic voltammetry showed a distinct peak with a maximum at around −150 mV. For anodizing at −100 and −200 mV, nanowires with diameters of ca. 19 and 24 nm respectively were found to be grown. Moreover, photoluminescence and X-ray diffraction...