Schra, L. (author)An interlaboratory testing programme to evaluate the rising displacement test for stress corrosion crack (SCO growth investigations was carried out within the framework of the "Measurements and Testing" programme of the European Community under BCR contract nr. MATI CT 930038. The contribution of the NLR to the project consisted of testing of...report 1996
- document
-
Schra, L. (author), Kolkman, H.J. (author)The SCC resistances of three damage tolerant aluminium sheet materials were determined by means of the ASCOR (Automated Stress COrrosion Ring) test. The conventional damage tolerant sheet material 2024-T3 was used as reference. The SCC resistance of 8090-T81 turned out to be only slightly lower than the SCC resistance of 2024-T3. In contrast,...report 1991
- document
-
Schra, L. (author), 't Hart, W.G.J. (author), Boogers, J.A.M. (author)Outdoor corrosion and stress corrosion tests were conducted on Al-Li plate and sheet materials for 3 and almost 5 years respectively. The results can be summarized as follows: Corrosion: Peak aged XXXA-T651 (8090-T651) exhibited greater exfoliation corrosion resistance than 2024-T351 and 2324-T39 plate. 2091-T3 and 2024-T3 sheet were found to be...report 1990
- document
-
't Hart, W.G.J. (author), Schra, L. (author)A comparative experimental investigation was done on the advanced plate alloys 7010-T651 from ALCAN and 7150-T6E189 from ALCOA. The mechanical properties, fracture toughness and corrosion properties were determined. The most notable finding was the excellent fracture toughness of alloy 7150-T6E189 combined with a high tensile strength. The...report 1982
- document
-
't Hart, W.G.J. (author), Kolkman, H.J. (author), Schra, L. (author)The Jominy end-quench test was applied to rods of the alximinium alloys T010 and X TO9I to obtain a decreasing cooling rate over the length of the rods. After heat treating to a high strength T6 and an overaged TT condition the corrosion properties and the microstructure were determined related to the cooling rate. No influence of cooling rate...report 1982
- document
-
Wanhill, R.J.H. (author)Flight simulation fatigue crack propagation tests with gust spectrum loading were carried out on laminates of (i) aluminium alloy 2024-T3/carbon-epoxy, (ii) aluminium alloy 7475-T761/carbon-epoxy and (iii) titanium alloy Ti-6Al-4V/carbon-epoxy with nominal weight savings of 30% and 40% as compared to equivalent 2024-T3 Alclad and 7475-T761...report 1982
- document
-
Schra, L. (author), Huisman, H.N. (author)An experimental investigation was carried out into the applicability of various corrosive environments for stress corrosion crack initiation testing of high strength aluminium alloys using constant strain loaded tuning fork type specimens. The effect of surface preparation was also involved. The most important findings were that salt-chromate...report 1981
- document
-
Wanhill, R.J.H. (author)Flight simulation fatigue crack propagation tests on 202U-T3 and 7475-T761 aluminum alloy sheet were carried out using a gust spectrum representative of the load history of an under wing skin in a transport aircraft. The investigation included tests at several design stress levels and in environments of laboratory air and air plus water spray....report 1980