Behavior of reinforcing steel and reinforced concrete undergoing stray current

Currents flowing along paths not being elements of a purpose-built electric circuit, are called stray currents. Various types of reinforced concrete structures (such as viaducts, bridges and tunnels) in the neighborhoods of railways may be subjected to stray current leaking from the rails. In these cases the concrete pore solution acts as an...

Incorporating cracking of concrete on chloride ingress and service life modeling of concrete structures

Chloride induced reinforcement corrosion is the most common degradation mechanisms for reinforced concrete structures. The service life of concrete structures is normally predicted by estimating the rate of chloride ingress and the necessary time to initiate reinforcement corrosion. Normally, chloride ingress is modeled as a diffusive process in...

Effect of corrosion on the fatigue service-life on steel and reinforced concrete beams

Chloride-induced corrosion is a point of big concern in reinforced concrete (RC) structures. To monitor the actual health and to predict the remaining service-life of structures, it is important to understand the structural behaviour and the failure mechanism of structures exposed to chlorides under fatigue loading conditions. A beam test,...

Corrosion and protection in reinforced concrete: Pulse cathodic protection: an improved cost-effective alternative

Corrosion and protection in reinforced concrete. Pulse cathodic protection: an improved cost-effective alternative. The aim of the research project was to study the possibilities for establishing a new or improved electrochemical method for corrosion prevention/protection for reinforced concrete. The main objective was to develop an alternative...

Experimental investigations on macro cell corrosion in chloride-contaminated concrete

Chloride-induced reinforcement corrosion in concrete is characterised by the action of so-called macrocells. The associated localised form of corrosion results from the strong electrochemical interaction between the relatively small pitting sites acting as anodes and the large passive steel areas acting as cathodes. The existence of macrocell...