Study of solidification cracking during laser welding in advanced high strength steels: A combined experimental and numerical approach

Preventing solidification cracking is an essential prerequisite for the safety of a welded structure. An undetected solidification crack has the potential to cause premature failure during service. Two conditions generated by a weld thermal cycle are responsible for the initiation of solidification cracks. The first is the presence of excessive...

Microstructural evolution of white and brown etching layers in pearlitic rail steels

The formation of White (WEL) and Brown Etching Layers (BEL) on rail raceways during service causes the initiation of microcracks which finally leads to failure. Detailed characterization of the WEL and the BEL in a pearlitic rail steel is carried out from micrometer to atomic scale to understand their microstructural evolution. A...

Evaluation of solidification cracking susceptibility during laser welding in advanced high strength automotive steels

Solidification cracking susceptibility during laser welding was studied experimentally and numerically in advanced high strength steel sheets, namely transformation-induced plasticity (TRIP) and dual phase (DP) steel. Using the same heat input, laser bead-on-plate welding was carried out on single sided clamped specimens at various starting...

Study of solidification cracking in advanced high strength automotive steels

Advanced high-strength steels (AHSS), which are increasingly used in the automotive industry, meet many functional requirements such as high strength and crash resistance. Some of these steels contain high amounts of alloying elements, which are required to achieve the necessary mechanical properties, but render these steels susceptible to weld...

Experimental evidence of liquid feeding during solidification of a steel

Sufficient liquid feeding under constrained solidification conditions like, those experienced in welding and casting, is vital to avoid solidification cracking. We present the results of unique in-situ experimental observations of liquid feeding in a solidifying steel melt pool. Liquid feeding was observed in the inter-cellular regions during...

Hot cracking investigation during laser welding of high-strength steels with multi-scale modelling approach

Hot cracking during laser welding of advanced high-strength steels is reported to be a serious problem by automotive manufacturers. In this work, hot cracking susceptibilities of transformation-induced plasticity (TRIP) and dual-phase (DP) steels are studied based on a multi-scale modelling approach. Transient temperatures measured from...