The material grown in a scanning electron microscope by electron beam-induced deposition (EBID) using Pt(PF3)4 precursor is shown to be electron beam sensitive. The effects of deposition time and postgrowth electron irradiation on the microstructure and resistivity of the deposits were assessed by transmission electron microscopy, selected area diffraction, and four-point probe resistivity measurements. The microstructure, notably the platinum nanocrystallite grain size, is shown to evolve with electron fluence in a controllable manner. The resistivity was observed to decrease as a result of postgrowth electron irradiation, with the lowest observed value of 215±15????cm. The authors demonstrate that electron beam-induced changes in microstructure can be caused using electron fluences similar to those used during the course of EBID and suggest that the observed effects can be used to tailor the microstructure and functionality of deposits grown by EBID in situ without breaking vacuum.