On page 452, column 1 (lines 12?23) reads: H2 and CO chemisorption show an uptake of 0.91 molH2 molPd?1 and 0.61 molCO molPd ?1, respectively (Table 1, Supporting Information S6). Considering a 1:1 CO/Pd stoichiometry,32 the dispersion from CO chemisorption (D?CO) equals 61%, in a reasonable agreement with the dispersion from TEM (D?TEM 70%; Supporting Information S9).32 While H2 chemisorption is not effective for a determination of the metal dispersion of Pd nanoparticles due to the formation of a stable bulk hydride with larger particles (2.6 nm),32 a comparison of the H2 uptake and D?CO would correspond to approximately three hydrogen atoms per surface Pd.

The direct conversion of CO₂to CH₃OH represents an appealing strategy for the mitigation of anthropogenic CO₂emissions. Here, we report that small, narrowly distributed alloyed PdGa nanoparticles, prepared via surface organometallic chemistry from silica-supported Ga^IIIisolated sites, selectively catalyze the hydrogenation of CO₂to CH₃OH. At 230 °C and 25 bar, high activity (22.3 mol_MeOHmol_Pd^-1h^-1) and selectivity for CH₃OH/DME (81%) are observed, while the corresponding silica-supported Pd nanoparticles show low activity and selectivity. X-ray absorption spectroscopy (XAS), IR, NMR, and scanning transmission electron microscopy-energy-dispersive X-ray provide evidence for alloying in the as-synthesized material. In situ XAS reveals that there is a dynamic dealloying/realloying process, through Ga redox, while operando diffuse reflectance infrared Fourier transform spectroscopy demonstrates that, while both methoxy and formate species are observed in reaction conditions, the relative concentrations are inversely proportional, as the chemical potential of the gas phase is modulated. High CH₃OH selectivities, across a broad range of conversions, are observed, showing that CO formation is suppressed for this catalyst, in contrast to reported Pd catalysts.