The electrochemical nitrogen reduction reaction (NRR) is a promising alternative to the current greenhouse gas emission intensive process to produce ammonia (NH₃) from nitrogen (N₂). However, finding an electrocatalyst that promotes NRR over the competing hydrogen evolution reaction (HER) has proven to be difficult. This difficulty could potentially be addressed by accelerating the electrocatalyst development for NRR by orders of magnitude using high-throughput (HTP) workflows. In this work, we developed a HTP gas diffusion electrode (GDE) cell to screen up to 16 electrocatalysts in parallel. The key innovation of the cell is the use of expanded Polytetrafluoroethylene (ePTFE) gas diffusion layers (GDL) which simplifies the handling of catalyst arrays compared to carbon fabrics and enables sufficient N₂ mass transport. We demonstrate the robustness of the HTP workflow by screening 528 bimetallic catalysts of composition AB (A,B = Ag, Al, Au, Co, Cu, Fe, Mn, Mo, Ni, Pd, Re, Ru, W) for NRR activity. None of the materials produced ammonia significantly over background level which emphasizes the difficulty of finding active electrocatalysts for NRR and narrows down the search space for future studies.

Hydrogen permeable electrodes can be utilized for electrolytic ammonia synthesis from dinitrogen, water, and renewable electricity under ambient conditions, providing a promising route toward sustainable ammonia. The understanding of the interactions of adsorbing N and permeating H at the catalytic interface is a critical step toward the optimization of this NH3 synthesis process. In this study, we conducted a unique in situ near ambient pressure X-ray photoelectron spectroscopy experiment to investigate the solid-gas interface of a Ni hydrogen permeable electrode under conditions relevant for ammonia synthesis. Here, we show that the formation of a Ni oxide surface layer blocks the chemisorption of gaseous dinitrogen. However, the Ni 2p and O 1s XPS spectra reveal that electrochemically driven permeating atomic hydrogen effectively reduces the Ni surface at ambient temperature, while H2 does not. Nitrogen gas chemisorbs on the generated metallic sites, followed by hydrogenation via permeating H, as adsorbed N and NH3 are found on the Ni surface. Our findings suggest that the first hydrogenation step to NH and the NH3 desorption might be limiting under the operating conditions. The study was then extended to Fe and Ru surfaces. The formation of surface oxide and nitride species on iron blocks the H permeation and prevents the reaction to advance; while on ruthenium, the stronger Ru-N bond might favor the recombination of permeating hydrogen to H2 over the hydrogenation of adsorbed nitrogen. This work provides insightful results to aid the rational design of efficient electrolytic NH3 synthesis processes based on but not limited to hydrogen permeable electrodes.