We have investigated in detail properties of hybrid polyelectrolyte-anion exchange membranes (AEMs) having different amounts of a guanidinium-modified poly(allylamine hydrochloride) (PAH-Gu) derivative (2, 5, and 8 wt%). The presence of guanidinium groups at the membrane surface was confirmed by XPS. For 2 and 5 wt% the blended membranes are homogeneous, while at 8 wt% segregation is observed by AFM. The membrane permselectivity and ionic electrical resistance for phosphate reduce upon incorporation of the PAH-Gu in the membrane, reflecting an increased co-ion (H⁺ and Na⁺) permeation. We conclude that PAH-Gu loaded in the AEM favors an interaction with phosphate. In electrodialysis, using sodium sulfate and sodium dihydrogen phosphate at equal concentrations in the source phase a slight preference for phosphate was observed. Our work shows that this facile membrane fabrication procedure shows great potential in terms of tuning the membrane properties. One way to boost selective ion transport could be by increasing the number of functional groups in the membrane.

In this study we describe a novel and simple method to couple covalently poly (maleic anhydride-alt-1-alkenes) to γ-alumina nanofiltration membranes for the first time. The 1-alkenes varied from 1-hexene, 1-decene, 1-hexadecane to 1-octadecene. The grafting reaction was between the reactive anhydride moieties of the polymer and surface hydroxyl groups, resulting in highly stable bonds. The modified membranes were investigated for their permeation and rejection performance of Sudan Black (SB, M_w 457 Da) in either toluene or ethyl acetate (EA) solution, and very high rejections (> 90%) and high permeation flux were observed compared to unmodified membranes. Initially, the SB in toluene solution was found to bind strongly to the surface hydroxyl groups of the unmodified membranes, an effect not observed in EA solution.

During the last decade, the synthesis and application of metal-organic framework (MOF) nanosheets has received growing interest, showing unique performances for different technological applications. Despite the potential of this type of nanolamellar materials, the synthetic routes developed so far are restricted to MOFs possessing layered structures, limiting further development in this field. Here, a bottom-up surfactant-assisted synthetic approach is presented for the fabrication of nanosheets of various nonlayered MOFs, broadening the scope of MOF nanosheets application. Surfactant-assisted preorganization of the metallic precursor prior to MOF synthesis enables the manufacture of nonlayered Al-containing MOF lamellae. These MOF nanosheets are shown to exhibit a superior performance over other crystal morphologies for both chemical sensing and gas separation. As revealed by electron microscopy and diffraction, this superior performance arises from the shorter diffusion pathway in the MOF nanosheets, whose 1D channels are oriented along the shortest particle dimension.

The electrochemical behavior of three differently charged drug molecules (zwitter-ionic acetylcarnitine, bi-cationic succinylcholine and tri-cationic gallamine) was studied at the interface between two immiscible electrolyte solutions. Tetramethylammonium was used as a model mono cationic molecule and internal reference. The charge and molecular structure were found to play an important role in the drug lipophilicity. The studied drugs gave a linear correlation between the water – octanol (logP_octanol) partition coefficients and the electrochemically measured water – 1,2-dichloroethane (logP_DCE) partition coefficients. Comparison with tetraalkylammonium cations indicating that the correlation between logP_octanol and logP_DCE is molecular structure dependent. The highest measured sensitivity and lowest limit of detection were found to be 0.543 mA·dm³·mol^{− 1} and 6.25 μM, respectively, for the tri-cationic gallamine. The sensitivity for all studied ions was found to be a linear function of molecular charge. The dissociation constant of the carboxylic group of zwiter-ionic acetylcarnitine was calculated based on voltammetric parameters and was found to be 4.3. This study demonstrates that electrochemistry at the liquid – liquid interface is powerful technique when it comes to electroanalytical or pharmacokinetic drug assessment.

Affinity layers play a crucial role in chemical sensors for the selective and sensitive detection of analytes. Here, we report the use of composite affinity layers containing Metal Organic Frameworks (MOFs) in a polymeric matrix for sensing purposes. Nanoparticles of NH₂-MIL-53(Al) were dispersed in a Matrimid polymer matrix with different weight ratios (0-100 wt %) and drop-casted on planar capacitive transducer devices. These coated devices were electrically analyzed using impedance spectroscopy and investigated for their sensing properties toward the detection of a series of alcohols and water in the gas phase. The measurements indicated a reversible and reproducible response in all devices. Sensor devices containing 40 wt % NH₂-MIL-53(Al) in Matrimid showed a maximum response for methanol and water. The sensor response time slowed down with increasing MOF concentration until 40 wt %. The half time of saturation response (τ_0.5) increased by ∼1.75 times for the 40 wt % composition compared to devices coated with Matrimid only. This is attributed to polymer rigidification near the MOF/polymer interface. Higher MOF loadings (≥50 wt %) resulted in brittle coatings with a response similar to the 100 wt % MOF coating. Cross-sensitivity studies showed the ability to kinetically distinguish between the different alcohols with a faster response for methanol and water compared to ethanol and 2-propanol. The observed higher affinity of the pure Matrimid polymer toward methanol compared to water allows also for a higher uptake of methanol in the composite matrices. Also, as indicated by the sensing studies with a mixture of water and methanol, the methanol uptake is independent of the presence of water up to 6000 ppm of water. The NH₂-MIL-53(Al) MOFs dispersed in the Matrimid matrix show a sensitive and reversible capacitive response, even in the presence of water. By tuning the precise compositions, the affinity kinetics and overall affinity can be tuned, showing the promise of this type of chemical sensors.

The in situ electrochemical growth of Cu benzene-1,3,5-tricarboxylate (CuBTC) metal-organic frameworks, as an affinity layer, directly on custom-fabricated Cu interdigitated electrodes (IDEs) is described, acting as a transducer. Crystalline 5-7 μm thick CuBTC layers are grown on IDEs consisting of 100 electrodes with a width and a gap of both 50 μm and a height of 6-8 μm. These capacitive sensors are exposed to methanol and water vapor at 30 °C. The affinities show to be completely reversible with higher affinity toward water compared to methanol. For exposure to 1000 ppm methanol, a fast response is observed with a capacitance change of 5.57 pF at equilibrium. The capacitance increases in time followed diffusion-controlled kinetics (k = 2.9 mmol s^-0.5 g^-1 _CuBTC). The observed capacitance change with methanol concentration follows a Langmuir adsorption isotherm, with a value for the equilibrium affinity K_e = 174.8 bar^-1. A volume fraction f_MeOH = 0.038 is occupied upon exposure to 1000 ppm of methanol. The thin CuBTC affinity layer on the Cu-IDEs shows fast, reversible, and sensitive responses to methanol and water vapor, enabling quantitative detection in the range of 100-8000 ppm.

A major challenge in nanotechnology is that of determining how to introduce green and sustainable principles when assembling individual nanoscale elements to create working devices. For instance, textile nanofinishing is restricted by the many constraints of traditional pad-dry-cure processes, such as the use of costly chemical precursors to produce nanoparticles (NPs), the high liquid and energy consumption, the production of harmful liquid wastes, and multistep batch operations. By integrating low-cost, scalable, and environmentally benign aerosol processes of the type proposed here into textile nanofinishing, these constraints can be circumvented while leading to a new class of fabrics. The proposed one-step textile nanofinishing process relies on the diffusional deposition of aerosol NPs onto textile fibers. As proof of this concept, we deposit Ag NPs onto a range of textiles and assess their antimicrobial properties for two strains of bacteria (i.e., Staphylococcus aureus and Klebsiella pneumoniae). The measurements show that the logarithmic reduction in bacterial count can get as high as ca. 5.5 (corresponding to a reduction efficiency of 99.96%) when the Ag loading is 1 order of magnitude less (10 ppm; i.e., 10 mg Ag NPs per kg of textile) than that of textiles treated by traditional wet-routes. The antimicrobial activity does not increase in proportion to the Ag content above 10 ppm as a consequence of a "saturation" effect. Such low NP loadings on antimicrobial textiles minimizes the risk to human health (during textile use) and to the ecosystem (after textile disposal), as well as it reduces potential changes in color and texture of the resulting textile products. After three washes, the release of Ag is in the order of 1 wt %, which is comparable to textiles nanofinished with wet routes using binders. Interestingly, the washed textiles exhibit almost no reduction in antimicrobial activity, much as those of as-deposited samples. Considering that a realm of functional textiles can be nanofinished by aerosol NP deposition, our results demonstrate that the proposed approach, which is universal and sustainable, can potentially lead to a wide number of applications.