This work is intended to provide a better understanding about the properties and roles of the reaction rim in an alkali-silica reaction. A simplified calcium-alkali-silicate system was created to simulate the multiple interactions among reactive silica, alkaline solution and portlandite near the aggregate surface during the formation and evolution of the reaction rim in an alkali-silica reaction. A transport barrier preventing the migration of calcium and silicate through itself was found on the interface between the alkali silicate and the calcium hydroxide. The barrier was mainly composed of calcium alkali silicate with silicon-oxygen organizations of Q2 and Q3 according to the results of 29Si nuclear magnetic resonance, the calcium to silica mole ratio ranging from 0.22 to 0.53 and the alkali to silica ratio ranging from 0.20 to 0.26 based the location of the elemental compositional analysis and the storage period of the system.@en

This work aims at providing a better understanding of the mechanical properties of the reaction rim in the alkali-silica reaction. The elastic modulus of the calcium alkali silicate constituting the reaction rim, which is formed at the interface between alkali silicate and Ca(OH)2 in a chemically-idealized system of the alkali-silica reaction, was studied using nano-indentation. In addition, the corresponding calcium to silica mole ratio of the calcium alkali silicate was investigated. The results show that the elastic modulus of the calcium alkali silicate formed at the interface increased with the increase of the calcium to silica mole ratio and vice versa. Furthermore, the more calcium that was available for interaction with alkali silicate to form calcium alkali silicate, the higher the calcium to silica mole ratio and, consequently, the higher the elastic modulus of the formed calcium alkali silicate. This work provides illustrative evidence from a mechanical point of view on how the occurrence of cracks due to the alkali-silica reaction (ASR) is linked to the formation of the reaction rim. It has to be highlighted, however, that the simplified calcium-alkali-silicate system in this study is far from the real condition in concrete.@en