Advanced (ultra)high-strength steels that utilise bcc-fcc microstructures are appealing solutions for producing a combination of high strength and deformability. However, they are also susceptible to hydrogen embrittlement (HE). As larger less stable retained austenite (RA) can impair mechanical performance, its size and morphology are critical factors for achieving and maintaining the desired properties. Here, we present a combined experimental–density functional theory (DFT) study on HE with medium-carbon direct-quenched and partitioned (DQ&P) martensitic steels with varying vol% and film-thickness of RA, showing significantly improved HE resistance as a function of bcc-enrichment and increasing RA film-thickness. DFT reveals low attraction of hydrogen in bcc-Fe with Al, implying a stronger push towards fcc. Furthermore, the solubility of hydrogen increases dramatically with the carbon-enrichment of fcc-Fe when hydrogen and carbon are second neighbours. The theoretical results explain the observed differences in hydrogen diffusion, trap density, and the consecutively lower HE in Al-DQ&P over Si-DQ&P. Our combined experimental and theoretical study thus highlights the important interplay of bcc and fcc phases and H-uptake within austenite-containing carbon steels.

In the present study, the effect of Niobium (Nb) on the hydrogen embrittlement resistance of Quenched and Partitioning (Q&P) steel is investigated. For this purpose, the hydrogen uptake level and its impact on the mechanical properties of a Nb-free and a 0.024 wt% Nb Q&P steel are thoroughly analysed. The hydrogen trapping capacity is evaluated via thermal desorption spectroscopy (TDS). In-depth analysis of the desorption kinetics at different heating rates allows identification and quantification of the available trapping sites. The hydrogen embrittlement sensitivity of both steels is characterized using static and dynamic tensile tests. The addition of Nb results in an increase of the hydrogen concentration by more than 25%. The larger hydrogen content in the Nb steel, as a result of the higher fraction of grain boundaries/interphases, gives rise to a more severe embrittlement of the Nb steel compared to the Nb-free one. In addition to the larger hydrogen fraction in the Nb Q&P steel, the larger retained austenite fraction of low stability is detrimental due to the larger fraction of high carbon martensite formed when straining. This results in higher susceptibility to hydrogen embrittlement of the Nb microalloyed steel due to the brittle character of the high carbon martensite that forms easily during straining. Under dynamic loading conditions, the hydrogen embrittlement of both steels is minimal, which is attributed to a reduced hydrogen diffusion and the suppression of the transformation induced plasticity (TRIP) effect due to adiabatic heating.

The hydrogen induced damage of generic Fe-C-Ti and Fe-C-V ferritic alloys was investigated to assess the influence of precipitates on the hydrogen sensitivity of a material. The precipitates, formed during heat treatment, were evaluated by scanning transmission electron microscopy (STEM). The hydrogen/material interaction was evaluated by: 1) melt and hot extraction to determine the total and diffusible hydrogen content, respectively, 2) permeation experiments to calculate the diffusion coefficient, 3) thermal desorption spectroscopy to determine the hydrogen trapping characteristics of the materials. Furthermore, two different types of hydrogen induced damage were evaluated, i.e. hydrogen assisted cracking and blistering, resulting from electrochemical hydrogen charging with and without the application of an external load, respectively. Evaluation of the hydrogen induced damage and the role of the precipitates was performed by combining optical microscopy, scanning electron microscopy (SEM), and electron backscatter diffraction (EBSD). An important though divertive role of diffusible hydrogen is observed in both damage mechanisms for the investigated microstructures. On the one hand, a large amount of diffusible hydrogen compared to strongly trapped hydrogen promotes hydrogen assisted cracking of materials, while on the other hand, the blistering phenomenon is delayed under such conditions.