Previous research has consistently found that introducing metastable retained austenite (RA) as a second phase retards the failure of steel under fatigue. However, the reasons for this benefit are not understood. Accordingly, the properties of RA most advantageous to resist fatigue are not known. Within this context, this paper examines the interaction between second-phase RA and short fatigue crack growth in a steel processed via quenching and partitioning, using quasi in situ electron backscatter diffraction experiments. Results show that most RA transforms into martensite under the plastic strain surrounding the crack. They also reveal various mechanisms whereby RA transformation delays short fatigue crack propagation; transformation-induced crack closure (TICC), crack deflection and branching, and roughness-induced crack closure (RICC). Crack deflection and branching are driven by a tendency of cracks to propagate towards transformed RA, which is against the previous assumptions in the literature. Furthermore, the impact of crack deflection/branching on retardation is more powerful than that of TICC acting alone. Microstructures including second-phase RA should avoid RA-lean areas and promote elongated RA grains, with relatively large size, and major axis normal to the preferential crack growth direction. Untransformed RA within the plastic zone (i.e. overstabilized) does not contribute to crack retardation.

Quenching & Partitioning (Q&P) steels owe their good strength-ductility combinations to the martensite/austenite (α’/γ) mechanical interactions and to the formation of mechanically-induced martensite (α′_mech) through the transformation-induced plasticity (TRIP) effect. An essential role is played by carbon, whose distribution among the phases can be modified through the Q&P route. This study presents a methodology to systematically and quantitatively examine the influence of the α’/γ mechanical interactions on the overall work hardening of the steel with respect to the role of carbon in the martensite. The methodology rests on the generation of a 3D micro-mechanical model that allows to derive, by crystal plasticity simulations, the overall response of a mechanically-stable α’/γ virtual microstructure. In combination with theoretical knowledge on hardening, the comparison between the experimental and simulated mechanical responses enables the quantification of the influence of the martensite carbon content and distribution on the overall TRIP strengthening contribution of the steel. The approach is applied to two low carbon Q&P-processed α’/γ microstructures of similar initial volume fractions of austenite and α′_mech formation kinetics with strain, but one containing a Nb-microaddition and displaying improved strength-ductility values. It is shown that the martensite strength and work hardening ability might additionally enhance or partially counteract the strengthening contribution from the austenite-to-α′_mech transformation during uniaxial loading. The results of this study highlight that the processing-dependent properties of the carbon-depleted martensite should be considered in the optimization of Q&P processed steels.

The article focuses on the effect of alloying and microstructure on formability of advanced high strength steels (AHSSs) processed via quenching and partitioning (Q&P). Three different Q&P steels with different combination of alloying elements and volume fraction of retained austenite are subjected to uniaxial tensile and Nakajima testing. Tensile mechanical properties are determined, and the forming limit diagrams (FLDs) are plotted. Microstructure of the tested samples is analyzed, and dramatic reduction of retained austenite fraction is detected. It is demonstrated that all steels are able to accumulate much higher amount of plastic strain when tested using Nakajima method. The observed phenomenon is related to the multiaxial stress state and strain gradients through the sheet thickness resulting in a fast transformation of retained austenite, as well as the ability of the tempered martensitic matrix to accumulate plastic strain. Surprisingly, a Q&P steel with the highest volume fraction of retained austenite and highest tensile ductility shows the lowest formability among studied grades. The latter observation is related to the highest sum of fractions of initial fresh martensite and stress/strain induced martensite promoting formation of microcracks. Their role and ability of tempered martensitic matrix to accumulate plastic deformation during forming of Q&P steels is discussed.

In present study, the potential of Niobium (Nb) to improve the mechanical properties of Quenched and Partitioning (Q&P) steels is investigated. To this purpose, the effect of the addition of Nb on the microstructure and mechanical properties of a Q&P steel was thoroughly analysed with special attention on the thermal stability of the retained austenite. The mechanical properties of the Nb Q&P steel were determined using static and dynamic tensile tests and compared to the properties of a Nb free Q&P steel. Additionally, the effect of test temperature was quantified by static and dynamic tests in the temperature range from −40 °C to +80 °C. It was found that the Nb induced grain refinement together with the stabilising effect of Nb on the retained austenite, resulted in an excellent low temperature behaviour of the Nb Q&P steel. Additionally, the high temperature, dynamic behaviour of the Nb micro-alloyed steel was improved with respect to the Nb free steel due to the presence of a large fraction of retained austenite with low thermal stability.

Because of their excellent combination of strength and ductility, quenching and partitioning (Q & P) steels have a great chance of being added to the third generation of advanced high strength steels. The large ductility of Q & P steels arises from the presence of 10% to 15% of retained austenite which postpones necking due to the transformation induced plasticity (TRIP) effect. Moreover, Q & P steels show promising forming properties with favourable Lankford coefficients, while their planar anisotropy is low due to a weak texture. The stability of the metastable austenite is the key to obtain tailored properties for these steels. To become part of the newest generation of advanced high strength steels, Q & P steels have to preserve their mechanical properties at dynamic strain rates and over a wide range of temperatures. Therefore, in the present study, a low-Si Q & P steel was tested at temperatures from -40 °C to 80 °C and strain rates from 0.001 s^-1 to 500 s^-1. Results show that the mechanical properties are well-preserved at the lowest temperatures. Indeed, at -40 °C and room temperature, no significant loss of the deformation capacity is observed even at dynamic strain rates. This is attributed to the presence of a large fraction of austenite that is so (thermally) stable that it does not transform in the absence of deformation. In addition, the high stability of the austenite decreases the elongation at high test temperatures (80 °C). The additional adiabatic heating in the dynamic tests causes the largest reduction of the uniform strain for the samples tested at 80 °C. Quantification of the retained austenite fraction in the samples after testing confirmed that, at the highest temperature and strain rate, the TRIP effect is suppressed.