Direct ink writing of vascularized self-healing cementitious composites

Wan, Z.; Xu, Y.; He, S.; Chen, Y.; Xie, J.; Šavija, B.

doi:10.1016/j.cemconcomp.2023.105295

Direct ink writing of vascularized self-healing cementitious composites

Title

Direct ink writing of vascularized self-healing cementitious composites

Author

Wan, Z. (TU Delft Materials and Environment)
Xu, Y. (TU Delft Materials and Environment)
He, S. (TU Delft Materials and Environment)
Chen, Y. (TU Delft Materials and Environment)
Xie, J. (TU Delft Materials and Environment)
Šavija, B. (TU Delft Materials and Environment)

Date

2023

Abstract

Direct ink writing of cementitious materials can be an alternative way for creating vascular self-healing concrete by intentionally incorporating hollow channels in the cementitious matrix. In this study, a 3D-printable fibre reinforced mortar was first developed. Three groups of specimens were fabricated using direct ink writing, where the two top and bottom printing layers were printed with different printing directions. The macrostructure of the hardened specimens was studied using CT scanning. Four-point bending tests were carried out to investigate the initial flexural strength and the strength recovery after healing with injected epoxy resin. Furthermore, water permeability test was used to evaluate the healing potential of the samples. The results from CT scanning show that printing direction influences the actual volumes of hollow channels and the volume of small pores which are a consequence of the deposition process. The hollow channels of all samples were squeezed by the upper layers during the printing process, and the longitudinally printed samples were the most affected. When printing direction changes from longitudinal to transverse, the initial flexural strength decreases. Similarly, the average permeability of the cracked samples increases when the printing direction changes from longitudinal to transverse. Although the healing effectiveness regarding flexural strength is remarkable for all specimens, it was only possible to perform a single healing process as hollow channels were then blocked by the epoxy resin. The rough surface of the hollow channels is inferred to make it difficult to extract the epoxy resin out of the specimens.

Subject

3D printing
Printing direction
Self-healing
Vascular network

To reference this document use:

http://resolver.tudelft.nl/uuid:b3b8ecab-1b44-415e-b5ee-152750d80d5e

DOI

https://doi.org/10.1016/j.cemconcomp.2023.105295

ISSN

0958-9465

Source

Cement and Concrete Composites, 144

Part of collection

Institutional Repository