Cracking of SHCC due to reinforcement corrosion

Reinforcement corrosion is the most important deterioration mechanism affecting reinforced concrete infrastructures. After corrosion starts, expansive pressures are exerted onto the surrounding concrete, causing cracking and spalling of the cover concrete. The amount of cover cracking can possibly be reduced by using strain hardening...

Simulation of dynamic behavior of quasi-brittle materials with new rate dependent damage model

Stress-based nonlocal model, Damage, Rate dependency, Dynamic crack-branching Abstract. In concrete often complex fracture and fragmentation patterns develop when subjected to high straining loads. The proper simulation of the dynamic cracking process in concrete is crucial for good predictions of the residual bearing capacity of structures in...

Experimental and numerical study on cement paste degradation under external sulfate attack

External sulfate attack is one of the situations that may cause gradual but severe damage in cementitious materials, which may lead to cracking, increased permeability and strength loss. In this paper, thin-walled hollow cement paste cylinders with a wall thickness of 2.5mm were made considering the slow penetration process of sulfate ions under...

Induction healing of concrete reinforced by bitumen-coated steel fibres

Cracking in concrete structures compromises the durability and functionality of the structures themselves. Different kinds of self-healing concretes, less or more sophisticated, have been developed in the past ten years to overcome early cracks in structures. An experimental study of a novel self-healing concrete is presented. Bitumen, used as...

Effect of Post-Fire Curing on the Residual Mechanical Properties of Fire-Damaged Self-Compacting Concrete

Concrete is recognized for being a fire-resistant construction material. At elevated temperatures concrete can, however, undergo considerable damage such as strength degradation, cracking, and explosive spalling. In recent decades, reuse of fire-damaged concrete structures by means of developing techniques to repair the degraded material has...

Algorithm for Non-proportional Loading in Sequentially Linear Analysis

Sequentially linear analysis (SLA) is an alternative to the Newton-Raphson method for analyzing the nonlinear behavior of reinforced concrete and masonry structures. In this paper SLA is extended to load cases that are applied one after the other, for example first dead load and then wind load. It is shown that every nonlinear analysis step can...

The influence of moisture on the fracture behaviour of concrete loaded in dynamic tension

Dynamic tests demonstrate an extensive rate effect on the tensile strength as well as the post-peak behaviour beyond loading rates of about 50 GPa/s. One of the possible explanations for the observed rate effects on the fracture behaviour is enhanced resistance by moisture in the pores. To study the influence of the moisture content and pore...