Determining the decomposition voltage of Cu(In_1-xGa_x)Se₂

Partial shading of CIGS modules can lead to permanent damage of the module in the shaded area. This is caused by harmful reverse bias voltages in the shaded area which lead to reverse bias induced defects, also known as wormlike defects. A lot is already known about the origin and propagation of wormlike defects. However, the fundamental...

How the absorber thickness influences the formation of reverse bias induced defects in CIGS solar cells

When a PV module is partially shaded, the shaded solar cells operate in a reverse bias condition. For Cu(In,Ga)Se2 cells this condition can cause defects that irreversibly reduce the output of these cells and the full module. In order to design robust shade-tolerant CIGS modules details need to be known of the conditions at which these...

Degradation of CIGS solar cells

Thin film CIGS solar cells and individual layers within these solar cells have been tested in order to assess their long term stability. Alongside with the execution of standard tests, in which elevated temperatures and humidity levels are used, the solar cells have also been exposed to a combination of elevated temperature and humidity and...