- document
-
Laméris, J. (author)The effect of the environment on the fatigue behaviour and residual strength of ARALL-3 has been studied using three types of specimens, varying in structural complexity. In addition to the reference ambient air condition, specimens were aged and/or fatigue loaded in hot/humid air or in sump tank fluid. Environmental fatigue loading of door...report 1994
- document
-
Moss, A.C. (author), 't Hart, W.G.J. (author)This investigation examined carbon/epoxy and aramide/epoxy composites in interlaminar shear and in open-hole tensile tests at 90 to the unidirectional fibre orientation. Epoxy resin was also tested under tension. Photomicroscopy and the S.E.M. were used to study the fracture surfaces. Wet tests were performed to investigate the influence of...report 1986
- document
-
van Leeuwen, H.P. (author)The literature concerning the application of fracture mechanics to the growth of creep cracks is discussed. As an introduction it is shown that linear elastic fracture mechanics have been applied successfully to the residual strength of brittle materials crack growth due to stress corrosion and crack growth due to fatigue. Next the methods are...report 1983
- document
-
Schra, L. (author), Faber, J. (author)An experimental investigation was carried out into the applicability of various corrosive environments for stress corrosion crack propagation testing of high strength aluminium alloys using double cantilever beam specimens. Testing under atmospheric conditions was used as a reference. It was found that stress corrosion crack growth under...report 1981
- document
-
Nederveen, A. (author), de Jong, J.B. (author)The influence of the approximation of the lower end of the load spectrum was investigated by comparative tests using the Basic F-27 test programme and an extended version, containing three times more cycles per flight. Crack growth was studied on notched sheet specimens made of Alclad 202U-T3 and Alclad TOT5-T6. Fatigue life tests were done on...report 1981
- document
-
van der Hoeven, W. (author), Schra, L. (author)The influence of sheet thickness (2 mm and 10 mm) and the influence of laminating (5x2 ram) on the fatigue crack growth properties of the aluminium alloy AL 7010-T 73651 were investigated. Both constant amplitude loading and flight simulation loading were applied. All 2 mm and 10 mm thick sheets were machined from a 150 mm thick plate, i.e....report 1981
- document
-
't Hart, W.G.J. (author), Schra, L. (author)The Al-Zn-Mg-Cu alloy 7050 produced by Alcoa is a typical plate and forging alloy because of its low quench sensitivity. In order to compare this alloy with the earlier tested plate alloy 7010 an experimental programme was performed involving tensile, fracture toughness, and fatigue testing. In addition stress corrosion crack initiation and...report 1980
- document
-
Bartelds, G. (author)The applicability of finite element methods to the analysis of cracks was studied in three phases. In the first phase the available methods for the calculation of elastic stress intensity data for cracks of arbitrary shape using finite element techniques were evaluated. The indirect energy release method using virtual crack front variation was...report 1979
- document
-
Wanhill, R.J.H. (author)A study was made of environmental fatigue crack propagation in 2.5 mm thick Ti-6A1-4V sheet conforming to AMS 4911, and 2.2 mm thick IMI 3l8 conforming to BS TA 10. The environments were dry argon, normal air, distilled water and 3.5 ^ aqueous NaCl. There were three alloy/orientation combinations: Ti-6A1-4V L-T, IMI 3l8 L-T and IMI 318 T-L. Test...report 1975
- document
-
Bartelds, G. (author), Nederveen, A. (author)Aluminium sandwich paaiels provided with carbon-epoxy uniaxial reinforcing strips were fatigued and subsequently tested for residual strength, Although both analysis ajid fatigue tests indicate that the crack tip zone is affected onlywhen the zone is in the immediate vicinity of a stiffener the reinforcement considerably increases crack...report 1974