On the Relationship between the Chromium Concentration, the Z-Phase Formation and the Creep Strength of Ferritic-Martensitic Steels

Journal article (2018)

Authors

H. Yu Novel Aerospace Materials - Aerospace Engineering
W. Xu Northeastern University China, Novel Aerospace Materials - Aerospace Engineering
S. van der Zwaag Novel Aerospace Materials - Aerospace Engineering
Research Group
Novel Aerospace Materials (Aerospace Engineering) (TU Delft)
Copyright: © 2018 H. Yu, W. Xu, S. van der Zwaag
DOI: https://doi.org/10.1002/srin.201800177
Microstructure Chromium concentration Ferritic-martensitic steels steel Z-phase
More Info
expand_more

Published Date

2018

Language

English

Reuse Rights

Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.

Faculty

Aerospace Engineering

Department

Aerospace Structures & Materials

Research Group

Novel Aerospace Materials

Abstract

In this study, the long term creep strength behavior of commercial heat resistant martensitic/ferritic steels with Cr levels ranging from 1 to 15 wt% is analyzed by linking their computed equilibrium compositions to their creep properties. At lower Cr levels, the calculated strength due to precipitation hardening agrees well with the experimental results. At high chromium levels and longer exposure times, an accelerated strength loss due to the formation of Z-phase precipitates has been reported. The accelerated strength loss is computationally analyzed and a correlation between accelerated strength loss and Z-phase formation is confirmed. A study is made to explore the option of adjusting the chemical composition of existing high-chromium steels to reduce the driving force for Z-phase formation. However, no proper composition ranges are found which combine a high Cr concentration with a significantly lower driving force for Z-phase formation.