To increase the utilization of used tires, reduce carbon emissions and improve asphalt pavement performance, SBS/TB crumb rubber modified asphalt binder was designed, which was enhanced by SBS and terminal blend (TB) crumb rubber. SBS/TB crumb rubber modified asphalt binder was prepared by mixing 0 %, 10 %, and 15 % TB crumb rubber with 2 % and 3 % SBS, respectively. This study investigated the microstructure, thermal stability and rheological properties of SBS/TB crumb rubber modified asphalt binder. The Spearman correlation coefficient is introduced to analyze the correlation of microstructural, thermodynamic and rheological parameters. The results showed that SBS and TB crumb rubber were uniformly dispersed in asphalt binder without agglomeration phenomenon. In addition, the interaction between SBS and TB crumb rubber resulted in the formation of cross-links between the polymer and the asphalt binder, significantly improving the storage stability and the thermal stability of the modified asphalt binder. The pyrolysis mechanism of the modified asphalt binder is One-dimension diffusion or One-dimension phase boundary. With the addition of SBS and TB crumb rubber, the rheological, high-and-low temperature properties of modified asphalt binder are improved. Finally, microstructural, thermodynamic and rheological parameters have an extremely strong correlation by Spearman correlation coefficient analysis.

In order to explore the feasibility and efficacy of reed-fiber-modified bitumen (RFMB), three lengths and three dosages of reed fibers were selected to modify bitumen and bituminous mortar, while the physicochemical properties of RFMB and RFMB mortar were analyzed. In this work, FTIR spectroscopy was employed to characterize the chemical impact of fiber on bitumen. The viscidity and rheology of RFMB and the tensile strength of RFMB mortar were evaluated using a Brookfield viscometer, dynamic shear rheometer, and monotonic tensile test. The results showed that adding fibers primarily affects the physical structure rather than the chemical composition of bitumen, confirmed by FTIR spectroscopy. RFMB viscosity increased with higher fiber dosage and fiber length. Rheological evaluations showed an enhanced complex shear modulus for RFMB, suggesting improved performance at higher temperatures but increased stiffness at lower temperatures, with the latter indicating reduced flexibility. RFMB also demonstrated superior fatigue and rutting resistance, albeit with compromised stress sensitivity. Tensile tests on RFMB mortar highlighted significant improvements, especially with longer fibers, while shorter 0.4 mm fibers showed modest reinforcement effects, possibly due to uneven distribution during sample preparation.