The effect of the presence of an anodic film and hybrid sol-gel coating loaded with corrosion inhibitors was evaluated as a strategy for enhanced barrier and active corrosion protection of aluminium alloy 2024-T3. In this study, AA2024-T3 specimens were anodized in a modified sulphuric-citric acid bath (SCA) as the first layer of a corrosion protective multilayer system and subsequently protected by the application of silica-based hybrid sol-gel coatings. These coatings were doped with LiNO3 and Ce(NO3)3 as corrosion inhibitors and studied in comparison with the inhibitor-free sol-gel coating in terms of morphology, composition and corrosion protection of intact and scribed specimens. The anodized AA2024-T3 with an overlaying inhibitor-free sol-gel coating showed the highest impedance modulus during long-term immersion in 0.1 mol·L−1 NaCl aqueous solution. Active corrosion protection of scribed coated specimens was studied by exposure to a 0.5 mol·L−1 NaCl solution and evaluated by surface analytical techniques. The addition of Li- and Ce-based salts into the hybrid sol-gel formulation showed active corrosion protection compared to the inhibitor-free scribed hybrid sol-gel coating. The Ce-doped sol-gel coating showed less visual corrosion and higher active corrosion protection than the Li-containing one during the long-term immersion test in 0.5 mol·L−1 NaCl. Present findings reveal that the combination of the anodic/hybrid sol-gel layers on AA2024-T3 enhances the corrosion protective properties barrier properties of both stand-alone systems and the incorporation of Li- and Ce-based inhibitors provide active corrosion.@en

Plasma electrolytic oxidation (PEO) has been targeted as an eco-friendly alternative technology to conventional chromic acid anodizing (CAA) for corrosion protection of aluminium alloys in the aircraft industry. However, conventional PEO technology implies high energy consumption. Flash-PEO coatings (≤10 μm) produced in short treatment times (≤ 5 min) constitute a feasible way to overcome this limitation. Nevertheless, the long-term corrosion resistance is compromised, thus requiring novel sealing post-treatments. The present work studies the effect of stand-alone hybrid sol-gel (HSG) and Ce-doped hybrid sol-gel (HSG–Ce) coatings as a sealing post-treatment to evaluate the long-term corrosion resistance of Flash-PEO coatings on aluminium alloy (AA) 2024-T3. The characterization of the PEO, HSG, and HSG-Ce coatings was performed by scanning electron microscopy, X-ray diffraction, water contact angle, dry adhesion tests (ISO 2409), optical profilometry and Fourier transform infrared spectroscopy. The corrosion behaviour was assessed by electrochemical impedance spectroscopy up to 21 days (3.5 wt% NaCl). Active corrosion protection was assessed by immersion tests of artificially scratched coatings. Present findings reveal that low-energy-cost Flash-PEO coatings were successfully formed on AA2024-T3 alloy. Both HSG and HSG-Ce coatings were homogeneously formed on Flash PEO coating. Regarding the corrosion resistance, HSG-Ce showed significant scratch protection during 21 days of immersion in 3.5 wt% NaCl. The results suggest that, while the release of Si and Ce from the coating provided corrosion protection, NO3−release promoted localized corrosion phenomena in the scribe. This was associated with the preferential pitting corrosion phenomena at the Cu-rich intermetallic compounds instead of forming a thick and stableNO3−-rich passive layer.@en

Zinc aluminium (Zn-Al) and lithium aluminium (Li-Al) – layered double hydroxides (LDH) coatings with incorporated inhibitors (Li−, Mo− and W−based) were successfully synthesized on AZ31 Mg alloy. Zn−Al LDH W and Li−Al LDH Li showed the highest corrosion resistance and were selected for further evaluation. SEM cross−section examination revealed a bi−layer structure composed of an outer part with loose flakes and a denser inner layer. XRD, FTIR, and XPS analysis confirmed the incorporation of the inhibitors. Post−treatments with corrosion inhibitors containing solutions resulted in the selective dissolution of the most external layer of the LDH coating, reducing the surface roughness, hydrophilicity and paint adhesion of the layers. Active corrosion properties were confirmed by SVET evaluation for the Zn−Al LDH W coating. The proposed active corrosion mechanism involves the ion−exchange of aggressive Cl− ions, deposition of hydroxides and competitive adsorption of W−rich corrosion inhibitors.@en