A new route towards strong yet ductile metals via architecting heterogeneities in both structure and metastability is presented. Such heterogeneities are generated and manipulated in a standard stainless steel using a heterogeneous phase transformation (het-PT) strategy, in which focused laser patterning is applied to stimulate site-specific phase transformations. The het-PT processed steel contains periodically arranged stripes of strong martensite and ductile austenite with different grain sizes and metastability. The resulting structural heterogeneity leads to a desirable strain gradient and heterogeneous deformation-induced martensitic transformation during deformation, which effectively accommodate strain localization and enhance work hardening capability in the het-PT-processed steel. These unique features result in an enhanced balance between strength and ductility, outperforming both homogeneously ultrafine-grained and coarse-grained counterparts. The het-PT strategy is expected to be applicable to tailoring structural heterogeneity and metastability in other steels and metals.

For decades, grain boundary engineering has proven to be one of the most effective approaches for tailoring the mechanical properties of metallic materials, although there are limits to the fineness and types of microstructures achievable, due to the rapid increase in grain size once being exposed to thermal loads (low thermal stability of crystallographic boundaries). Here, we deploy a unique chemical boundary engineering (CBE) approach, augmenting the variety in available alloy design strategies, which enables us to create a material with an ultrafine hierarchically heterogeneous microstructure even after heating to high temperatures. When applied to plain steels with carbon content of only up to 0.2 weight %, this approach yields ultimate strength levels beyond 2.0 GPa in combination with good ductility (>20%). Although demonstrated here for plain carbon steels, the CBE design approach is, in principle, applicable also to other alloys.