Multiphase bainitic steels, as a third generation of advanced high strength steels, show promising properties for automotive applications. Understanding the micro-mechanisms of damage initiation during plastic deformation is a key to further mechanical properties enhancement. The topological effect of martensite as a second phase constituent on local damage nucleation activity is significant. This effect has been studied in two different martensite banded microstructures produced by two various annealing cycles. The postmortem damage analysis by a scanning electron microscope on uniaxial loaded samples, revealed more damage nucleation along the dispersed and fragmented martensite phase within martensite banded regions. More pronounced strain partitioning was observed in coarse bainitic grains between adjacent martensite blocks. It is shown that the fracture strain is not controlled by local damage activities, implying that earlier damage initiation or an increased volume fraction of voids does not give rise to a reduced ductility.@en

Recently, the third generation of advanced high strength steels (AHSSs) show promising properties for automotive applications. The improvement of macroscopic mechanical performance is not feasible without a deep understanding of the micromechanical behavior and failure micro-mechanisms involved during its response under various loading conditions. In this study, a uniaxial tensile test is conducted on a low silicon bainitic steel with second phase constituents (martensite and carbides). A comprehensive image processing on SEM micrographs is performed in order to quantify the damage evolution as a function of plastic deformation. A new methodology is examined to address the correlation between crystallographic orientation and damage initiation. In this multiphase steel, it appears that orientation dependence of damage initiation is blurred by the presence of different phases and hence there is not an obvious preferential orientation from where damage has initiated.@en