Plasmon-induced photocatalysts hold great promise for solar energy conversion owing to their strong light-harvesting ability and tunable optical properties. However, the complex process of interfacial extraction of hot carriers and the roles of metal/semiconductor interfaces in plasmonic photocatalysts are still not clearly understood. Herein, the manipulation of the interface between a plasmon metal (Au) and a semiconductor (rutile TiO₂) by introducing an interfacial metal oxide (Al₂O₃) is reported. The resulting Au/Al₂O₃/TiO₂ exhibits remarkable enhancement in photocatalytic water oxidation activity compared with Au/TiO₂, giving an apparent quantum efficiency exceeding 1.3% at 520 nm for photocatalytic water oxidation. Such an interfacial modulation approach significantly prolongs the lifetime of hot carriers in the Au/TiO₂ system, which conclusively improves the utilization of hot carriers for plasmon-induced water oxidation reaction upon irradiation. This work emphasizes the essential role of the interfacial structure in plasmonic devices and provides an alternative method for designing efficient plasmonic photocatalysts for solar energy conversion.

Lead-free inorganic halide perovskites have triggered appealing interests in various energy-related applications including solar cells and photocatalysis. However, why perovskite-structured materials exhibit excellent photoelectric properties and how the unique crystalline structures affect the charge behaviors are still not well elucidated but essentially desired. Herein, taking inorganic halide perovskite Cs₃Bi₂Br₉ as a prototype, the significant derivation process of silver atoms incorporation to induce the structural transformation from Cs₃Bi₂Br₉ to Cs₂AgBiBr₆, which brings about dramatic differences in photoelectric properties is unraveled. It is demonstrated that the silver incorporation results in the co-operated orbitals hybridization, which makes the electronic distributions in conduction and valence bands of Cs₂AgBiBr₆ more dispersible, eliminating the strong localization of electron–hole pairs. As consequences of the electronic structures derivation, exhilarating changes in photoelectric properties like band structure, exciton binding energy, and charge carrier dynamics are verified experimentally and theoretically. Using photocatalytic hydrogen evolution activity under visible light as a typical evaluation, such crystalline structure transformation contributes to a more than 100-fold enhancement in photocatalytic performances compared with pristine Cs₃Bi₂Br₉, verifying the significant effect of structural derivations on the exhibited performances. The findings will provide evidences for understanding the origin of photoelectric properties for perovskites semiconductors in solar energy conversion.