Fibre optic (FO) sensors are becoming increasingly popular for different applications in structural monitoring. Among their excellent properties, a strong interest for this type of sensors are represented by the possibility of embedding FOs inside composite components. In this case, one of the factors that significantly influence the efficiency of the whole Structural Health Monitoring (SHM) system is the interfacial adhesion between FO sensors and the host material. The main objective of this work is to investigate the interfacial adhesion between embedded fibre optic sensors and epoxy matrix to find the best type of optical fibre to be used in epoxy matrices to produce smart composites. Four types of optical fibres with different diameters and coatings (i.e. polyimide, polyacrylate and ormoceramic) were used. Pull-out tests were carried out and different methods were used to obtain the composite/optical fibre interfacial properties. Finally, an optical microscopy and Scanning Electron Microscopy (SEM) analysis were performed to characterize the fibre/matrix interfaces. It was found that the optical fibre that presented the highest energy required for interface rupture and, consequently, less invasiveness to the host material was the ormoceramic fibre with the smallest diameter.

@en

The main objective of this work is to study the effect of chemical treatment on the thermal properties of hybrid natural fiber-reinforced composites (NFRCs). Different chemical treatments [i.e., alkalized and mixed (alkalized+ silanized)] were used to improve the adhesion between the natural fibers (jute, ramie, sisal, and curauá) and the polymer matrix. A differential scanning calorimetry, thermogravimetry, and a dynamic mechanical analysis were performed to study the thermal properties of hybrid NFRC. It was found that the chemical treatments increased the thermal stability of the composites. Scanning electron microscopy images showed that the chemical treatments altered the morphology of the natural fibers. A rougher surface was observed in case of alkali treated fiber, whereas a thin coating layer was formed on the fiber surface during the mixed treatment. However, for some fibers (i.e., sisal and rami), the chemical treatment has a positive impact on the composite properties, whereas for the jute and curauá composites, the best behavior was found for untreated fibers.

@en

The aim of this study is to assess the interlaminar adhesion of carbon-epoxy laminates under salt water condition. Carbon-epoxy laminate specimens were immersed in a salt water tank for 60 days. Some specimens were then dried at
room temperature for 280 days, until recovering their initial weight. Specimens were tested using the composite peel test, an adaptation of the floating roller peel tests for composite materials. The results showed a degradation of peel strength in some areas due to the ageing process. The drying process did not affect the test results. A scanning electron microscopic analysis carried out on the fracture surface of the specimens revealed a typical mode I failure microstructure. A mixture of matrix failure and fibre/matrix interfacial failure was observed in non-aged specimens. Finally, a chemical characterization of the fracture surfaces with energy-dispersive spectroscopy confirmed the penetration of salt water in regions near the edge of the specimens. A degradation of the fibre/matrix interface adhesion was observed in affected areas. Floating roller peel tests proved to be a fast and effective method to access the interlaminar adhesion performance of composite laminates.@en