The multiphase microstructure of carbide-free bainitic steels comprises bainitic ferrite laths, retained austenite with different morphologies, a minor fraction of carbides and so-called martensite-austenite areas, which partially transform during the last cooling step. While the other constituent received much attention, little is known about the structure of the martensite-austenite constituent in carbide-free bainitic steels. Thus, in this study, it was structurally and chemically investigated by high-resolution techniques such as transmission electron microscopy and atom probe tomography after preceded unambiguous identification by electron backscatter diffraction in conventional as well as transmission mode. The results, ranging from carbon segregation to cementite precipitation in the martensitic part, indicate strong auto-tempering during final cooling which is followed by aging. Also, some kind of structural modulation in the austenite belonging to the martensite-austenite areas was observed. Atom probe tomography revealed a heterogeneous carbon distribution, further supporting the findings by transmission electron microscopy.

In this work a carbide-free bainitic steel was examined by a novel correlative microscopy approach using transmission Kikuchi diffraction (TKD) and transmission electron microscopy (TEM). The individual microstructural constituents could be identified by TKD based on their different crystal structure for bainitic ferrite and retained austenite and by image quality for the martensite-austenite (M-A) constituent. Subsequently, the same area was investigated in the TEM and a good match of these two techniques regarding the identification of the area position and crystal orientation could be proven. Additionally, the M-A constituent was examined in the TEM for the first time after preceded unambiguous identification using a correlative microscopy approach. The selected area diffraction pattern showed satellites around the main reflexes which might indicate a structural modulation.