A submarine may have to operate for a period of time with local corrosion damage in the pressure hull if a suitable repair method is unavailable or too expensive for implementation. This paper describes collapse tests on twenty ring-stiffened aluminium cylinders, which were conducted to study the effect of corrosion damage on hull strength and stability. Artificial hull thinning was found to reduce the collapse strength of experimental models through high local stresses in the corroded region. Leading to early onset of yielding and inelastic buckling. Bending associated with the eccentricity due to one-sided thinning was found to further increase the local stresses in the hull. Overall collapse pressures were more severely affected by corrosion damage than interframe collapse pressures. The percentage reduction in overall collapse pressure, compared with intact experimental models, was found to be closely related to the percentage depth of thinning. The accuracy of conventional collapse pressure predictions for the experimental models was significantly better for intact than for corroded cylinders.@en

The effect of corrosion damage on overall collapse strength of submarine pressure hulls was studied experimentally. Ring-stiffened cylinders were machined from aluminium tubing and loaded to collapse under external pressure. In selected specimens, some of the outer shell material was machined away in large single patches, representing general corrosion. Other specimens had many smaller patches, representing corrosion pitting from the outside of the hull, followed by grinding. Large-amplitude out-of-circularity (OOC) was introduced by mechanical deforming selected cylinders. Clusters of artificial corrosion pits were found to have approximately the same effect on collapse pressure as equal-depth general corrosion covering the same region of plating. General corrosion was found to be most severe when it was "in-phase" with OOC, since, during pressure loading, high compressive stresses resulting from corrosion were compounded by compressive bending stresses associated with OOC, and furthermore, the corrosion tended to increase the geometric imperfection itself. On the other hand, out-of-phase corrosion reduced the effect of OOC, while at the same time, the thinning associated compressive stresses were counteracted by local tensile bending stresses associated with OOC, so that strength reductions were correspondingly smaller. Overall collapse pressures for corroded specimens were reduced by, on average, 0.85% for each 1% of shell thinning. That result is based on a linear approximation of the nonlinear relationship between thinning and collapse pressure. The linear trend-line, which was used to account for the experimental scatter, is based on specimens with 13 to 27% shell thinning, and with a variety of corrosion areas and OOC amplitudes.@en