The charge distributions in α-Na2UO4, Na3NpO4, α-Na2NpO4, Na4NpO5, Na5NpO6, Na2PuO3, Na4PuO5, and Na5PuO6 are investigated in this work using X-ray absorption near-edge structure (XANES) spectroscopy at the U-L3, Np-L3, and Pu-L3 edges. In addition, a Rietveld refinement of monoclinic Na2PuO3, in space group C2/c, is reported for the first time, and the existence of the isostructural Na2NpO3 phase is revealed. In contrast to measurements in solution, the number of published XANES data for neptunium and plutonium solid phases with a valence state higher than IV is very limited. The present results cover a wide range of oxidation states, namely, IV to VII, and can serve as reference for future investigations. The sodium actinide series show a variety of local coordination geometries, and correlations between the shape of the XANES spectra and the local structural environments are discussed herein.@en

Solid/liquid equilibria in the system UO2–ZrO2 are revisited in this work by laser heating coupled with fast optical thermometry. Phase transition points newly measured under inert gas are in fair agreement with the early measurements performed by Wisnyi et al., in 1957, the only study available in the literature on the whole pseudo-binary system. In addition, a minimum melting point is identified here for compositions near (U0.6Zr0.4)O2+y, around 2800 K. The solidus line is rather flat on a broad range of compositions around the minimum. It increases for compositions closer to the pure end members, up to the melting point of pure UO2 (3130 K) on one side and pure ZrO2 (2970 K) on the other. Solid state phase transitions (cubic-tetragonal-monoclinic) have also been observed in the ZrO2-rich compositions X-ray diffraction. Investigations under 0.3 MPa air (0.063 MPa O2) revealed a significant decrease in the melting points down to 2500 K–2600 K for increasing uranium content (x(UO2)> 0.2). This was found to be related to further oxidation of uranium dioxide, confirmed by X-ray absorption spectroscopy. For example, a typical oxidised corium composition U0.6Zr0.4O2.13 was observed to solidify at a temperature as low as 2493 K. The current results are important for assessing the thermal stability of the system fuel – cladding in an oxide based nuclear reactor, and for simulating the system behaviour during a hypothetical severe accident.@en

In the context of a comprehensive campaign for the characterisation of transmutation fuels for next generation nuclear reactors, the melting behaviour of mixed uranium-americium dioxides has been experimentally studied for the first time by laser heating, for Am concentrations up to 70 mol. % under different types of atmospheres. Extensive post-melting material characterisations were then performed by X-ray absorption spectroscopy and electron microscopy. The melting temperatures observed for the various compositions follow a markedly different trend depending on the experimental atmosphere. Uranium-rich samples melt at temperatures significantly lower (around 2700 K) when they are laser-heated in a strongly oxidizing atmosphere compressed air at (0.300 ± 0.005) MPa, compared to the melting points (beyond 3000 K) registered for the same compositions in an inert environment (pressurised Ar). This behaviour has been interpreted on the basis of the strong oxidation of such samples in air, leading to lower-melting temperatures. Thus, the melting temperature trend observed in air is characterized, in the purely pseudo-binary dioxide plane, by an apparent maximum melting temperature around 2850 K for 0.3 < x(AmO2) < 0.5. The melting points measured under inert atmosphere uniformly decrease with increasing americium content, displaying an approximately ideal solution behaviour if a melting point around 2386 K is assumed for pure AmO2. In reality, it will be shown that the (U, Am)-oxide system can only be rigorously described in the ternary U-Am-O phase diagram, rather than the UO2-AmO2 pseudo-binary, due to the aforementioned over-oxidation effect in air. Indeed, general departures from the oxygen stoichiometry (Oxygen/Metal ratios ≠ 2.0) have been highlighted by the X-ray Absorption Spectroscopy (XAS). Finally, to help interpret the experimental results, thermodynamic computations based on the CALPHAD method will be presented.@en