Exploring more efficient and low-cost electrocatalysts to replace platinum (Pt) is highly desired to promote the practical hydrogen production through water splitting. Herein, a facile and effective strategy is proposed to fabricate self-standing Al₃Ni₂/Ni electrode with controlled phase composition and surface morphology, which is obtained by one-step electrochemical reduction of Al³⁺ on commercially available nickel in eutectic NaCl-KCl melt. Different from previously reported approaches, uniform Al₃Ni₂ monolith catalyst can directly grow onto Ni substrate. The deposit possesses unique three-dimensional (3D) cauliflower-like morphology comprising of nano- and microparticles due to the rapid nucleation rate during molten salt electrolysis. The as-fabricated Al₃Ni₂/Ni electrode can be directly used as the cathode to catalyze Hydrogen evolution reaction (HER). Impressively, it exhibits remarkable HER activity comparable to commercial Pt, including a low overpotential of 83.4 mV for a current density of 10 mA cm⁻², a small Tafel slope of 40.7 mV dec^-1, and excellent long-term stability over 36 h of continuous HER operation in 0.5 M H₂SO₄ solution. The intrinsic catalytic ability of Al₃Ni₂ with the unique hierarchical structure of nano/microsized grains can offer multiple effects, including massive exposed active sites, enhanced charge transfer and mass transport, and fast gas releasing that synergistically contribute to improving the electrocatalytic performance of HER. This work represents a highly promising approach to the design and one-step controllable fabrication of efficient and self-standing base metal electrode for electrocatalytic hydrogen production.

@en

The electrochemical behavior of Dy(III) and its co-reduction process with Zn(II) on a tungsten electrode were studied in eutectic NaCl-KCl melts at 700 °C by using a series of electrochemical techniques. The results indicate that the reduction of Dy(III) to Dy(0) is a diffusion controlled quasi-reversible process through a one-step reaction of exchanging three electrons. The diffusion coefficient of Dy(III) was calculated to be 1.7 × 10-5 cm2 s-1. Furthermore, the co-reduction of Dy(III) and Zn(II) on the tungsten electrode makes Dy(III) be reduced at more positive potentials due to the formation of various Dy-Zn intermetallic compounds. The electromotive force measurements were performed to determine the thermodynamic properties of the Dy-Zn intermetallic compounds, including the activities and relative partial molar Gibbs free energies of dysprosium in the two-phase coexisting state, as well as the standard formation Gibbs energies of Dy-Zn intermetallic compounds. Finally, potentiostatic electrolysis at -2.0 V was carried out in molten NaCl-KCl-DyCl3(1.0 mol%)-ZnCl2(1.0 mol%) at 700 °C for 11 h to prepare Dy-Zn alloy. X-ray diffraction and scan electron micrograph - energy dispersive spectrometry analyses showed that the obtained Dy-Zn alloy mainly comprised of DyZn2, as well as the minor phases of Dy2Zn17, DyZn3 and DyZn.@en