The development of new adhesives has allowed to expand the application of bonding into the most diverse industrial fields. This review article presents the commonly used experimental methods for the investigation of mechanical performance of adhesively bonded joints in the aerospace, wind energy, automotive and civil engineering sectors. In these sectors, due to their excellent intrinsic properties, composite materials are often used along with conventional materials such as steel, concrete and aluminium. In this context, and due to the limitations that the traditional joining techniques present, adhesive joints are an excellent alternative. However, standardized experimental procedures are not always applicable for testing representative adhesive joints in these industries. Lack of relevant regulations across the different fields is often overcome by the academia and companies’ own regulations and standards. Additional costs are thus mitigated to the industrial sectors in relation with the certification process which effectively can deprive even the biggest companies from promoting adhesive bonding. To ensure continuous growth of the adhesive bonding field the new international standards, focusing on actual adhesive joints’ performance rather than on specific application of adhesive joints are necessary.@en

This paper investigates the structural response of laminated glass beams under combined fire-exposure and sustained in-plane loading. This is done by means of experimental testing and Finite Element (FE) numerical modelling. Firstly, small-scale (1 m long) laminated glass beams are tested under thermal exposure and in-plane loading on a small fire resistance test furnace. From the test results it can be seen that laminated glass beams are able to sustain an imposed in-plane load for a time of 34–51 min before failing according to the limiting rate of deflection as defined in EN 1363–1:2012. It should be noted, however, that the observed failure times are strictly related to the boundary conditions applied in the test, i.e. the magnitude of mechanical loads (in this study a relatively small load of P = 1.15 kN was applied) and the presence of an inherent top zone protection, which may have positively affected the results. Secondly, additional FE thermo-mechanical simulations are performed to further investigate the mechanical response of the laminated glass beams under thermal exposure, with a focus on the effects of the top zone protection and the load magnitude on the performance of the examined laminated glass beams. From the FE study it can be seen that reducing the top zone protection (from 40 mm to 0 mm) results in a reduction in failure time from 45 min to 20 min, while increasing the load with a factor 5 (taking 30 mm top zone protection as a reference) results in a reduction of failure time from 32 to 18 min.@en