Copper telluride is a sort of solid waste generated from copper anode slime processing, from which the recovery of copper and particularly the high-value element of tellurium always encounter technical difficulties due to the complex physicochemical properties of tellurium. In this study, an efficient and compact process for copper telluride recycling has been developed. Efficient separation of tellurium and copper from copper telluride was achieved through a pressure oxidizing alkaline leaching process under the optimal conditions of 5 mol/L for NaOH concentration, 5:1 for liquid to solid ratio, 150 °C for temperature, 0.7 Mpa for system pressure, and 2 h for reaction time, by which over 95% of tellurium was selectively dissolved in the solution and copper was enriched in the solid phase mainly in the form of copper oxides. Tellurium was subsequently recovered as TeO2 by neutralization of the alkaline leaching solution with sulfuric acid to pH 4.5, delivering a TeO2 precipitation efficiency of over 95%. In general, the masses of tellurium and copper balanced well in both the liquid and solid phases for each step, and the overall recovery efficiencies of Te and Cu reached as high as approximately 91% and 98%, respectively.@en

Thallium is an emerging pollutant reported in wastewater along with the increasing mining and smelting of thallium-containing ores in recent years. The complete removal of Tl(I) from wastewater is of significant emergency due to its high toxicity and mobility, however, Tl(I) removal is always confronted with numerous technical difficulties because of the extremely low Tl(I) concentration in wastewater and the disturbances of many accompanying impurity ions. Adsorption is currently the most widely used method for Tl(I) removal on industrial scale and varied kinds of adsorbents such as Prussian blue analogues, biosorbents, and metal oxides have been developed. However, the adsorption process of Tl(I) is always affected by the co-existing cations, resulting in low Tl(I) removal efficiency. Recently, the development of a variety of novel adsorbents or ion sensors based on macrocyclic compounds for enrichment and accurate determination of trace Tl(I) in aqueous solutions exhibits great potential for application in Tl(I) removal from wastewater with high selectivity and process efficiency. This paper provides an overview of the adsorption methods for Tl(I) removal from wastewater with emphasis on complexation properties between varied types of adsorbents and Tl(I). Future directions of research and development of adsorptive Tl(I) removal from industrial wastewater are proposed.@en

In the present study, a novel process for effective recoveries of Te and Cu from copper telluride from anode slime processing in copper smelters was proposed. The process consists of two hydrometallurgical steps of atmospheric alkaline leaching for Cu and Te separation, and TeO2 precipitation with H2SO4 for Te recovery. The effects of NaOH concentration, liquid to solid ratio, temperature, H2O2 to Cu2Te mole ratio, and reaction time on the dissolution behavior of tellurium were investigated. A Te leaching efficiency of about 91% was obtained under the optimal experimental conditions. The results of thermodynamic and kinetic analysis indicate that a lower temperature is favorable for the dissolution of Te, and mass transfer inside the solid particle is the rate-determining step. In addition, a mechanochemical-assisted leaching was conducted, by which Te leaching efficiency was enhanced to approximately 93% with ball milling at 180 rpm for 5 h. After Te leaching, H2SO4 was utilized to adjust the pH value of the Te-containing alkaline leach solution to 4.5 for TeO2 precipitation. The crystallization of TeO2 can be completed by reacting for 1 h and the overall tellurium recovery has reached nearly 90%.@en