We have investigated the properties of interfaces between LaAlO3 films grown on SrTiO3 substrates singly terminated by TiO2. We used RF sputtering in a high-pressure oxygen atmosphere. The films are smooth, with flat surfaces. Transmission electron microscopy shows sharp and continuous interfaces with some slight intermixing. The elemental ratio of La to Al, measured by the energy dispersive X-ray technique, is found to be 1.07. Importantly, we find these interfaces to be non-conducting, indicating that the sputtered interface is not electronically reconstructed in the way reported for films grown by pulsed laser deposition because of the different interplays among stoichiometry, mixing, and oxygen vacancies.@en

Sputter deposition of oxide materials in a high-pressure oxygen atmosphere is a well-known technique to produce thin films of perovskite oxides in particular. Also interfaces can be fabricated, which we demonstrated recently by growing LaAlO3 on SrTiO3 substrates and showing that the interface showed the same high degree of epitaxy and atomic order as is made by pulsed laser deposition. However, the high pressure sputtering of oxides is not trivial and number of parameters are needed to be optimized for epitaxial growth. Here we elaborate on the earlier work to show that only a relatively small parameter window exists with respect to oxygen pressure, growth temperature, radiofrequency power supply and target to substrate distance. In particular the sensitivity to oxygen pressure makes it more difficult to vary the oxygen stoichiometry at the interface, yielding it insulating rather than conducting.@en